論文提要內容：在鈉鎢氧化物掺雜鍺(+4價)的製備過程中，其塊材表面長出絲狀鎢氧化物，內部含有顆粒方形單晶。當改變鍺含量，分別得到塊材、絲狀鎢氧化物、顆粒方形單晶。顆粒方形單晶和塊材的晶體結構為Na0.73WO3立方晶相，而絲狀鎢氧化物的晶體結構為WO2.625正交晶相 ; 在電性方面，當x ＝ 0.05 ~ 0.09 Na0.25GexWO3 的塊材，其低溫13 K有電阻轉折訊號，而絲狀鎢氧化物和顆粒方形單晶則無此訊號。同時高溫電性量測（300 K ∼ 380 K）結果顯示，顆粒方形單晶，高溫時有電阻轉折訊號 ; 在磁性方面，絲狀鎢氧化物在100 K有微小磁性轉折訊號。顆粒方形單晶則在50 K ∼ 280 K時有異常磁性行為。

Tungsten bronze wire single crystal and cubic crystal were attained through changing germanium concentration, the wires grew on the surface and the cubic crystals were inside the bulk. The crystalline structure of cubic crystal is cubic, the same as that of Na0.73WO3, the crystalline structure of wire is orthorhombic, the same as that of WO2.625 . The weak resistivity transition at 13K was observed for bulk Na0.25GexWO3 with germanium concentration ranging x from 0.05 to 0.09, but this transition were not observed for the cubic crystal and the wire. The resistivity transition also was occurred for the cubic crystal at high temperature ranging from 300 K to 400 K .The weak magnetism transition at 100 K was observed for Tungsten bronze wire. The anomalistic magnetism was observed for the cubic crystal at temperature ranging from 50 K to 280 K.

第一章 緒論
(一) 前言……………………………………………………………1
(二) 實驗背景與動機………………………………………………2
第二章 實驗裝置與量測系統……………………….4
2-1: 實驗裝置
（a） 高溫爐裝置………………………………………...…4
（b） 低溫電阻量測系統……………………………………5
（c） 磁性量測系統………………………………………..7
2-2：X-ray 粉末繞射分析
（a） X光繞射系統………………………………..………………7
（b） Rietveld精算法……………………………………………..9
第三章 樣品製備與量測方法…………………13
第四章 實驗結果與討論………………………17
4-1. 樣品X-ray繞射圖之結構分析……………………………..17
4-2. 樣品之電性分析……………………………………………..18
4-3. 樣品之磁性分析……………………………………..……...20
4-4. 樣品之高溫電性測量結果………………………………….21
4-5. 總結……………………………………………………….…22
參考文獻…………………………………………………………..55
圖表目錄
Fig. 1. Na0.25Ge0.09WO3單晶顆粒電子顯微鏡掃描照相…………....24
Fig. 2. 鈉鎢絲狀氧化物電子顯微鏡掃描照相………………….….25
Fig. 3. Na0.25GexWO3 X — ray粉末繞射圖………………………...26
Fig. 4. Na0.25Ge0.07WOx X - ray粉末繞射圖…………..………….. 27
Fig. 5. NaxGe0.07WO3 X - ray粉末繞射圖…………………………28
Fig. 6. Na0.73WO3 ICSD X - ray粉末繞射圖……………………......29
Fig. 7. Na0.73WO3 ICSD 立方晶相晶體結構圖……………………30
Fig. 8. Na0.25Ge0.09WO3單晶顆粒X - ray粉末繞射圖………….....31
Fig. 9. 絲狀鎢氧化物，Rietveld精算法彌合結果…………..……32
Fig. 10. Rietveld精算結果WO2.625正交晶相晶體結構…….….…33
Fig. 11. Na0.25GeyWO3 電性圖……………….……………….…..34
Fig. 12. Na0.25Ge0.07WOz 電性圖……………………………..…..35
Fig. 13. NaxGe0.07WO3 電性圖 …………………………………….36
Fig. 14. Na0.25GexWO3電性圖…………………………………..…..37
Fig. 15. Na0.25GexWO3 電性圖……………………………….….….38
Fig. 16. Na0.25Ge0.07WO3不同燒結條件之電性圖…………………39
Fig. 17. Na0.25Ge0.09WO3表面絲狀鎢氧化物電性圖…………..…..40
Fig. 18. Na0.25Ge0.09WO3顆粒單晶高溫電性圖……………….….41
Fig. 19. Na0.25Ge0.07WO3顆粒單晶電性圖…………………….….42
Fig. 20. Na0.2Ge0.09WO3顆粒單晶電性圖…………………….…..43
Fig. 21. Na0.3Ge0.09WO3顆粒單晶電性圖………………………..44
Fig. 22. Na0.25Ge0.09WO3表面絲狀鎢氧化物磁性圖……………..45
Fig. 23. Na0.25Ge0.09WO3顆粒單晶磁性圖………………………..46
Fig. 24. Na0.25Ge0.09WO3顆粒單晶磁性圖…………………….…..47
Fig. 25. Na0.25Ge0.09WO3顆粒單晶磁化率與溫度關係圖…………48
Fig. 26. Na0.2Ge0.09WO3顆粒單晶高溫電性圖………………..….49
Fig. 27. Na0.2Ge0.11WO3顆粒單晶高溫電性圖…………….…….50
Fig. 28. Na0.25Ge0.07WO3顆粒單晶高溫電性圖……………………51
Fig. 29. Na0.25Ge0.09WO3顆粒單晶高溫電性圖……………………52
Fig. 30. Na0.3Ge0.09WO3顆粒單晶高溫電性圖………………….…..53
表一Na0.25Ge0.09WO3表面絲狀鎢氧化物之各原子座標……………54

參考文獻
【1】 Ch. J. Raub, A. R. Sweedler, M. A. Jensen, S. Broadston, and B. T. Matthias, Phys. Rev. Lett. 13, 746 (1964)。
【2】 M. K. Wu, J. R. Ashburn, C. J. Torng, P. H. Hor, R. L. Meng, L. Gao, Z. J.Huang, Y. Q. Wang, and C. W. Chu, Phys. Rev. Lett. 58, 908 (1987)。
【3】 B. D. Bardeen, L. N. Cooper, and J. R. Schrieffer, Phys. Rev. Lett. 108, 1175 (1957)。
【4】 G. Xiao, F. H. Streitz, A. Garvin, Y. W. Du, and C. L. Chien, Phys. Rev. B 35, 8782 (1987)。
【5】 Howard R. Shanks, Solid State Commun. 15, 753 (1974)。
【6】 J.P. Remeika, T.H. Geballe, B.T. Matthias, A.S. Cooper, G.W. Hull, E.M. Kelly, Phys. Lett. 24A, 565 (1967)。
【7】 M. Apostal, and M, Popescu, Philos. Mag. Lett. 57, 305 (1988)。
【8】 M.Matsui, K. Ohmori, T.Shimizu, and M.Doyama, Physica B+C. 148, 432 (1987)。
【9】 I. W. Chen et al., Solid State Commun 63, 997 (1987)。
【10】 Wiseman P J, Dickens P Journal of Solid State Chemistry (1976)。