本論文是以熱差分析(DTA)、X光繞射及X光吸收光譜之延伸X光吸收光譜精細結構(EXAFS)分析技術，來對鈣鋁矽氧化物玻璃作特性與結構分析，並對樣品的製作與處理，均有詳細的介紹。經由改變SiO2的含量，在熱差分析的實驗中，我們發現玻璃的轉變溫度Tg會因SiO2含量增加而下降；X光繞射實驗驗證了本論文所使用的樣品確實是玻璃；對Ca K-edge的EXAFS作分析，發現到Ca的氧配位數會隨著SiO2含量的增加，從氧化鈣的6配位數變成3、4至5配位數。

In this research project we characterized to the structure and properties of calcium aluminosilicate glasses by the technique of DTA (Differential Thermal Analysis), X-ray diffraction and EXAFS (Extended X-ray Absorption Fine Structure) of X-ray absorption spectroscopy at the Ca K-edge. We made the glass samples. By changing the contents of SiO2 and found that the glass transition temperatures decreased with higher SiO2 contents. We verified our samples are all glasses by the X-ray diffraction. Finally, we analyzed the EXAFS of the Ca K-edge for the glass samples, and found the coordination number of oxygen around calcium changed from 3 to 5 with increasing SiO2 contents.

第一章、簡介
第一節、玻璃的定義 1
第二節、鈣鋁氧化物玻璃的簡介 3
第二章、X光吸收光譜細微結構原理簡介
第一節、X光吸收光譜內容 6
第二節、X光吸收光譜實驗環境 15
第三節、EXAFS原理 19
第四節、EXAFS的適用範圍 26
第三章、樣品製作及實驗步驟
第一節、樣品的製作與處理 32
第二節、玻璃轉變溫度(Tg)之測量 35
第三節、X光繞射實驗 39
第四節、X光吸收光譜實驗 39
第四章、熱差分析實驗及X光繞射結果
第一節、鈣鋁矽氧化物玻璃的玻璃轉變溫度 41
第二節、鈣鋁矽氧化物玻璃的X光繞射實驗結果 46
第五章、EXAFS數據處理及實驗結果
第一節、鈣鋁矽氧化物玻璃的X光吸收光譜數
據分析流程 51
第二節、鈣鋁矽氧化物玻璃中
鈣的 K-edge之EXAFS分析結果 60
第六章、結論 72
參考資料 74
附錄 77

[1] H. Rawson, Properties and Applications of Glass
(Elsevier Socience Publishers, New York, 1980).
[2] J. Wong and A. Angell, Glass Structure by
Spectroscopy (Dekker, New York, 1976)
[3] M. E. Lines, J. Appl. Phys., 60, 1472 (1986).
[4] M. E. Lines, J. Non-Cryst. Solids, 103, 279 (1988).
[5] M. E. Lines, J. B. MacChesney, K. B. Lyons, A. J.
Bruce, A.E. Miller, and K. Nassau, J. Non-Cryst.
Solids, 107, 251 (1989).
[6] L. G. Hwa, C. C. Chen, and S. L. Hwang, Chin. J.
Phys., 35, 78 (1997).
[7] L. G. Hwa, J. Raman Spectro., 29, 269 (1998).
[8] P. L. Higby, R. J. Ginther, I. D. Aggarwal, and
E. J. Friebele, J. Non-Cryst. Solids, 126, 209
(1990).
[9] 鄭伯昆,核子輻射與偵測 (亞東書局, 1989).
[10] D.E.Sayers¸E.A.Sterm and F.W.Lytle¸
Phys. Rev. Lett., 27¸1024 (1971).
[11] Douglas Vaughan, Center for X-ray Optics X-Ray
data booklet (Lawrence Berkeley Laboratory,
1986).
[12] B. K. Teo, EXAFS : Basic Principles and Data
Analysis (Springer-Verlag, 1986).
[13] H. Winick, S. Doniach, Synchrotron Radiation
Research (Plenum Press, 1988).
[14] D. C. Konigsberger, X-Ray Absorption,
principles,applications, technigues of EXAFS,
SEXAFS and XANES (R. Prins, Chem. Analysis
Vol. 92, Wiley, 1988).
[15] T. M. Hayes, J. B. Boyce, Solid State Physics
(Vol. 37, Academic Press, 1982).
[16] L. V. Azaroff, Rev. Mod. Phys., 35, 1012 (1963).
[17] C. C. Kuo, SRRC Commissioning (Second ICFS
School, Hsinchu, 1993).
[18] H. Wiedemann, Physics of Synchrotron Radiation
(Second ICFS School, Hsinchu, 1993).
[19] J. T. Sakurai, Advanced Quantum Mechanics
(Addison-Wesley, Reading, MA, 1967).
[20] E. Sevillano, H. Meuth, J. J. Rehr, Phys. Rev.
B, 20, 4908 (1979).
[21] 國科會精密儀器中心, 儀器總覽, P.109.
[22] B. K. Teo, P. A. Lee, J. Am. Chem. Soc., 101,
2815 (1979).
[23] Ziyu Wu, C. Romano, A. Marcelli, A. Mottana, G.
Cibin, G. Della Ventura, G. Giuli, P. Courtial and
D. B. Dingwell, Phys. Rev. B, vol. 60, 9216
(1999).
[24] 黃詩郎, 以振動光譜來研究鈣鋁氧化物玻璃之
結構 (輔仁大學物理研究所碩士論文，第五章).
[25] P. McMillan and B. Pirious, J. Non-Cryst. Solids,
55 (1983).
[26] 陳家駿, 鈣鋁氧化物玻璃紅外線吸收之研究 (輔
仁大學物理研究所碩士論文，第五章).
[27] James F. Shackelford, Introduction to Materials
Science for Engineers (Macmillan).
[28] 輔仁大學物理系華魯根教授實驗室