本研究可分為兩個部份，第一部份為合成有機高分子聚乙烯醇poly(vinyl alcohol)簡稱(PVA)/無機化合物CaCO3奈米複合材料；合成原理是先將PVA依照一定比例溶解在水中，在加入氫氧化鈣Ca(OH)2，並通入二氧化碳CO2使得氫氧化鈣變成碳酸鈣CaCO3。藉由CO2進入PVA的方式不同，來達到合成CaCO3粒徑的不同。
第二部份，對此材料進行一些物性測試。如: SEM、TGA、Uv-Vis以及拉力應用等測試。
本研究是利用化學反應，讓CaCO3在聚乙烯醇(PVA)中以極小顆粒形成且分散性佳；同時所製備的高分子奈米複合材料可發現碳酸鈣粒徑小於100nm，符合奈米材料的要求；另一方面，也希望我們所選擇的碳酸鈣和聚乙烯醇對生物是有益處的，而且聚乙烯醇是可以被生物分解的，能符合環境保護的問題，更祈盼未來能夠用聚乙烯醇來取代PVC(聚氯乙烯)。

This thesis can be divided into two parts. For the first part, a series of poly(vinyl alcohol)/CaCO3 Nano- composites were prepared. The synthesis principle is first dissolves PVA according to the certain proportion in the water,and Joins the calcium hydroxide, and passes over the carbon dioxide to cause the calcium hydroxide to turn the calcium carbonate. Because the carbon dioxide enters PVA the way to be different, achieves the synthesis calcium carbonate particle size the difference.
For the second part, thesis Nanocomposites were subsequently characterized by SEM,Vis-Uv,TGA and tensile force.

摘要…………………………………………………………………………3
Abstract………………………………………………………………4
誌謝 …………………………………………………………5
表目錄………………………………………………………………………8
圖目錄………………………………………………………………………9
第一章 緒論 ………………………………………………12
第二章 文獻回顧……………………………………………15
2.1 奈米技術的簡介…………………………………………………15
2.1.1 奈米技術製造原理… …………………………………………16
2.1.2奈米技術製的應用 ……………………………………………17
2.2 複合材料的介紹與主要的型態…………………………………18
2.3 碳酸鈣的介紹………………………………………………20
2.4 PVA的簡介 ……………………………………………………21
2.4.1 PVA的用途 ……………………………………………………22
2.4.2 PVA之一般特性 ………………………………………………23
2.5 碳酸鈣和聚乙烯醇 ……………………………………………24
2.5.1 碳酸鈣在塑膠中的應用………………………………………24
2.5.2 PVA/nana-CaCO3的應用………………………………………26
2.5.3 奈米碳酸鈣在橡膠的應用……………………………………27
2.5.4 PVA/Ag2S(12)的應用……………………………………27
第三章 實驗部份 ………………………………………………………29
第四章 結果與討論 ………………………………………………………33
4.1 凝集程度的測試及測量IR結果…………………………………33
4.2薄膜厚度…………………………………………………………36
4.3分散性……………………………………………………………38
4.4 穿透率試驗UV-Vis……………………………………………40
4.5 顆粒大小比較…………………………………………………46
4.6 TGA 熱分析儀…………………………………………………57
4.7 拉力測試………………………………………………………69
第五章 結論與展望 ………………………………………………………73
第六章 參考文獻…………………………………………………………74

1. 工業材料, 86年5月，125期。
2. 工業材料, 88年9月，153期。
3. 九十四年度教育部辦理技專校院發展學校重點特色專案補助計畫計畫名稱：可撓式顯示器奈米材料教學與研究專案計畫 徐新興教授
4. B. Li and W. Fan, Materials Research Bulletin 38 1567–1572 (2003)
5. X. F. Qian , J. Yin, J. C. Huang, Y. F. Yang, X. X. Guo and Z. K. Zhu, Materials Chemistry and Physics 68 95–97 (2001)
6. 長春化學(股)公司提供。
7. M. AVELLA , M. E. ERRICO, R. RIMEDIO, JOURNAL OF MATERIALS SCIENCE 39 6133–6136 (2004)
8. J. H. Chang, T. G. Jang, K. J. Ihn, W. K. Lee, and G. S. Sur
Journal of Applied Polymer Science, Vol. 90, 3208–3214 (2003)
9. D. LO´ PEZ, I. CENDOYA, F. TORRES, J. A. TEJADA, C. A. MIJANGOS, Journal of Applied Polymer Science, Vol. 82, 3215–3222 (2001)
10. J. XU, Y. Z. MENG, R. K. LI, Y. XU, A. V. RAJULU, Journal of Polymer Science: Part B: Polymer Physics, Vol. 749–755 (2003)
11. Y. Yin, J. f. Li, Y. C. Liu, and Z. Li, Journal of Applied Polymer Science, Vol. 96, 1394–1397 (2005)
12. S. W. Ali, S. A. R. Zaidi, Journal of Applied Polymer Science, Vol. 98, 1927–1931 (2005)
13. H. H. WANG, T. W. SHYR, and M. S. HU, Journal of Applied Polymer Science, Vol. 73, 2219–2226 (1999)
14. R. W. Oliver,「生物科技大未來」，美商麥格羅•希爾，台北（2000）。
15.,D.C. Lee, and L.W. Jang, Applied Polymer Science.,1996,61,1117.
16. C. L. Dong and W. J. Lee, J. Appl. Polym. Sci., 61, 1117 (1996)
17. F. Claudia, G. Marco, G. Silvia, R. Giacomo, A. V. Carlo and M. Bernardo, Polymer, 39, 2651 (1998)
18. Y. Kojima, A. Usuki, M. Kawasumi, A. Okada, Y. Fukushima, T. Kurauchi and O. Kamigaito, J. Mater. Res., 8, 1185 (1993)
19. F. Bergaya and F. Kooli, Clay Miner, 26, 33 (1991)
20. R. A. Vaia, H. Ishii and E. P. Giannelis, Chem. Mater., 5, 1694 (1993)
21. M. M. Alesaimi, J. Appl. Polym. Sci., 367 (1997)
22. A. Moet and A. Akelah, J. Mater. Sci., 28, 3589 (1996)
23. Y. Sugahara, S. Satokawa, K. Kuroda and C. Kato, Clays Clay Miner, 36, 343 (1988)
24. C. Kato, K. Kuroda and H. Takahara, Clays Clay Miner, 29, 294 (1981)
25. A. Moet and A. Akelah, Mater. Lett., 18, 97 (1993)
26. A. Akelah, A. Rehab, A. Selim and A. Agag, J. Mol. Cat., 94, 311 (1994)
27. A. Usuki, Y. Kojima, M. Kawasumi, A. Okada, Y. Fukushima, T. Kurauchi and O. Kamigaito, J. Mater. Res., 8, 1179 (1993)
28. Y. Kojima, A. Usuki, M. Kawasumi, A. Okada, T. Kurauchi and O. Kamigaito, J. Appl. Polym. Sci., 49, 1259 (1993)