本論文研究乃利用乳化聚合法自行合成出以不飽合聚酯樹脂與苯乙烯為共單體之反應性微膠顆粒(reactive microgels)，用以當作不飽和聚酯之抗體積收縮劑。並探討反應性微膠顆粒型LPA添加到不飽和聚酯系統之SEM微觀結構之觀測。
而蒙特納石黏土是另外一種特用添加劑，是經由Silane有機化改質而來的。並且探討蒙特納石黏土(Montmorillonite clay，MMT)添加到不飽和聚酯系統中，其聚合固化後三成份樣品之微觀結構與機械性質之影響。

This study is based on utilization of reactive microgels low additive profile，which were prepared by emulsion polymerization。Reactive microgel materials are composed of styrene/unsaturated polyester comonomer。Moreover，this study focus on effect of MMT in unsaturated polyester system。Then we would change styrene(ST)/unsaturated polyester(UP)/MMT ratio to investigate the influence of mechanical properties。

中文摘要………………………………………………………………..Ⅰ
英文摘要………………………………………………………………..Ⅱ
誌謝……………………………………………………………………..Ⅲ
目錄……………………………………………………………………..Ⅳ
圖表目錄………………………………………………………………..Ⅷ
第一章 緒論……………………………………………………………..1
1-1 不飽和聚酯(UP).………………………………………….1
1-2 增韌劑……………………………………………………..2
1-3 抗收縮劑…………………………………………………..3
1-4 反應性微膠顆粒…………………………………………..4
1-5 研究範疇…………………………………………………..6
第二章 文獻回顧………………………………………………………..7
2-1 反應性微膠顆粒(reactive microgels)………………..……...7
2-2 不飽和聚酯(UP)樹脂之合成……………………………...10
2-3 不飽和聚酯(UP)樹脂與苯乙烯(ST)之交聯共聚合反應…11
2-4 不飽和聚酯(UP)/樹脂/苯乙烯(ST)/抗收縮劑(LPA)三成
份系統之相溶性…………………………………………..14
2-5 不飽和聚酯硬化後的機械性質研究……………………...15
2-6 乳化聚合法………………………………………………...17
2-7 自由基聚合反應…………………………………………...26
2-8 黏土的特性………………………………………………...29
2-9 蒙特納石黏土之相關性質………………………………...30
第三章 實驗方法及設備………………………………………………32
3-1 原料………………………………………………………...32
3-2 三成份試片原料…………………………………………...33
3-2-1 不飽和聚酯樹脂(Unsaturated Polyester，UP)……….33
3-2-2 苯乙烯(Styrene，ST)………………………………….35
3-2-3 高溫起始劑(t-butyl peroxybenzoate，TBPB)…………36
3-3 特用添加劑………………………………………………...37
3-3-1 蒙特納石黏土(Montmorillonite clay，MMT)……….37
3-4 反應性微膠顆粒型LPA之合成…………………………..39
3-5 實驗儀器…………………………………………………...40
3-6 實驗步驟…………………………………………………...42
3-6-1 反應性微膠顆粒(reactive microgels)型LPA之合成...42
3-6-2 乳液乾燥………………………………………...........44
3-7 三成份試片製作…………………………………………...45
3-8 SEM微觀結構……………………………………………...47
3-8-1 ST/UP/Silane-treated MMT……………………………47
3-8-2 ST/UP/Reactive microgels……………………………..48
3-9 機械性質之量測…………………………………………...49
3-9-1 耐衝擊測試(Impact Test)……………………………..49
3-9-2 拉伸測試(Tension Test)…………………………….50
3-9-3 破壞韌性(Fracture toughness)………………………...51
3-9-4 波松比測試(Poisson’s ratio)………………………….52
3-9-5 破壞能量(Fracture energy)……………………………53
第四章 結果與討論……………………………………………………54
4-1 反應性微膠顆粒(reactive microgels)型抗收縮劑之合成...55
4-2 苯乙烯/不飽和聚酯樹脂/反應性微膠顆粒三成份系統
之微觀結構…………..……………………………………57
4-3苯乙烯/不飽和聚酯樹脂/蒙特納石黏土三成份系統之
微觀結構……………………………………………………63
4-4 特用添加劑(MMT)之機械性質……………………..…….69
4-4-1 耐衝擊測試………………………..………………….69
4-4-2 抗張強度測試…………..…………………………….72
4-4-3 破壞韌性測試………………………………………...78
4-4-4 波松比測試…………………………………………...82
4-4-5 破壞能量……………..……………………………….85
第五章 結論……………………………………………………………88
第六章 未來之工作……………………………………………………90
参考文獻………………………………………………………………..91
附錄A…………………………………………………………………..95
附錄B…………………………………………………………………..96
附錄C…………………………………………………………………..97

1、R.B.Burn,Polyester Molding Compounds,Marcel Dekker,Inc,New
York,1982
2、E. Martuscelli, P. Musto, G.. Ragosta, G. Scarinzi, and E. Bertotti,
J.Polym.Sci., Part B：Polym.Phys.,31,619(1993)
3、S.B. Pandit, and V.M. Nadkarni, Ind. Eng. Chem. Res.,33,2778(1994)
4、The B.F. Goodrich Co., WO93/21274(Oct. 28,1993)
5、Crc for Polymers Pty. Ltd., WO97/43339(Nov. 20,1997)
6、The B.F.Goodrich Co,Wo 93/21274(Oct.28,1993)
7、E.J. Bartkus and C.H Kroekel, Appl.Polym.Symp.,15, 113(1970)
8、K.E.Atkins,in”Sheet Molding Compound :Science and Technology”
.Ed., H.G. Kia, Hanser Publishers, New York,1993, Ch4.
9、V.A. Pattison, R.R. Hindersinn and W.T. Schwartz,J. Appl.Polym.Sci., 18,2763(1974)
10、V.A. Pattison, R.R. Hindersinn and W.T. Schwartz,J. Appl.Polym.Sci., 19,3045(1975)
11、L. Suspenp, D. Fourquier and Y. S. Yang,Polymer, 32(1991)
12、Y. J. Huang,and C. M. Liang, Polymer, 37,401(1996)
13、W.Li, L. J. Lee,and K.H. Hsu, Polymer, 41,711(2000)


14、C.B. Bucknall, l.K. Partidge and M.J. Phillips, Polymer, 32,636(1991)
15、L. Suspene, D. Fourquier and Y.S. Yang, Polymer,32,1593(1991)
16、C.P. Hsu, M. Kinkelaar, P. Hu and L.J. Lee. Polym.Eng.Sci.,31, 1450,
(1991)
17、Y.J Huang and C.M. Liang, Polymer, 37,401(1996)
18、Y.J. Huang, C.J. Chu, and J.P. Dong, J. Appl. Polym. Sci., 78,543
(2000)
19、Y.J. Huang, T.S. Chen, J.G. Huang, and F.H. Lee,J.Appl. Polym. Sci.,
89,3336(2003)
20、J.P. Dong, J.G. Huang, F.H. Lee, J.W. Roan,and Y.J. Huang,J.Appl.
Polym.Sci.,91,3388(2004)
21、L.Suspene,D.Fourquier,and Y.S.Yang,Polymer,32,1593(1991)
22、Y.J.Hung and C.C.Su,J.Appl Polym. Sci,55,323(1995)
23、Y.J.Huang and W.C.Jiang,Polymer,39,6631(1998)
24、Y.J.Huang, C.J.Chu, and J.P.Dong, J. Appl. Polym. Sci., 78,543(2000)
25、W.Funke,R.Kolitz,and W.Strachle,Makromol.Chem,.180,2797(1979)
26、W.Funke, Br. Polym J,21,107(1989)
27、W.Funke,Ger.Offen. 2746481,Bayer AG, inv, 1977
28、M.Miyata ,and W.Funke Makromol.Chem.184,755(1983)
29、Y.S.Yang and L.J.Lee,Polymer,29,1793(1988)
30、K.Horie,I.Mita,and H.Kambe,J.Polym.Sci.PartA-1:Polym. Chem.,7,
2561(1969)
31、江文慶,碩士論文,國立台灣科技大學，1996
32、Y.J.Huang and J.C.Horng,Polymer,39,3683(1998)
33、Y.J.Huang and L.D.Chen,Polymer,39,7049(1998)
34、W.D.Cook and O.Delatycki,J.Polym.Sci.,Polym.Phys.Ed.,12,2111
(1974)
35、W.D.Cook and O.Delatycki,J.Polym.Sci.,Polym.Phs.Ed.,12,1925，(1974)
36、Y.J.Huang, S.C.Lee,and J.P.Dong,J.Appl.Polym.Sci.,78,558(2000)
37、Y.J.Huang,T.S.Chen,J.G.Huang,andF.H.Lee,J.Appl.Polym.Sci.,89,
3347(2003)
38、J.P.Dong, J.G.Huang, F.H.Lee,J.W.Roam,and Y.J.Huang J.Appl.
Polym.Sci.,89,3347(2003)
39、彭俊昇,碩士論文,國立台灣科技大學,2000
40、C.C Wang, N.S. Yu, C.Y. Chen and J. F. Kuo, Polymer., 37,2509
(1996)
41、廖平喜,聚合物化學,高立圖書有限公司,台北,1997
42、H.R. Allcock and F.W. Lampe.,”Contemporary Polymer Chemistry”,
2nd Ed., Prentice Hall, Englewood Cliffs, New Jersey, 1990, p.50

43、A.R. Ubbelode and F.A.Lewis, Graphite and its Crystal
Compounds,Oxford Press,London, U.K.,1960
44、Akane Oakda, Arimitsu Usuki, Toshio Kurauchi, Osami
Kamigaito,Acs Symp,1995
45、百康奈米科技有限公司產品目錄
46、林仕笳，碩士論文，中國文化大學，2002
47、W.E.Worrall,”Clays and Ceramic Raw Materials,”2nd Ed.,Elsevier,
London(1986)
48、Izod Impact Strength Testing of Plastics，MatWeb Material Property Data
49、P.W.K. Lam, Polym, Eng. Sci., 29,609(1989)
50、C.W. Bucknall, I.K. Partridge , and M.J. Phillips, Polym, 32, 786
(1991)