臺灣博碩士論文加值系統

本實驗利用醇熱法合成五氧化二釩粉末及釹摻雜五氧化二釩粉末，以偏釩酸銨水溶液與乙二醇混合或添加硝酸釹，經120°C 加熱1 小時後，經由不同溫度煆燒而獲得五氧化二釩及釹摻雜的五氧化二釩，可產生粉末。本研究製備的粉末應用於光觸媒降解染料及當作電致變色之還原層材料。
當粉末經由煆燒300°C 時可以獲得斜方五氧化二釩。且在煆燒温度為400°C 時，可以獲得最小的尺寸，約為2-3 微米。釹摻雜五氧化二釩經由不同溫度煆燒，利用X-射線繞射分析，證明粉末組成為釩酸釹結構(NdVO4)。將NdVO4粉末應用在可見光照射時對亞甲基藍進行降解，效率最高可達67%。應用在電致變色上由光譜儀分析元件穿透率變化，電致色變在550 nm 以下可得最佳穿透差異性(ΔT%)為20.6%，光學密度差(ΔOD)為0.10。

This work prepares the vanadium pentoxide (V2O5) and the neodymiorm (Nd) doping V2O5 powders by a glycothermal method. The ammonium metavanadate was mixed with ethylene glycol or add to neodymiorm nitrate then heating at 120oC for 1hr, and the precipitates obtained. These precipitates were calcinated at different temperatures. And these powders applied in photocatalyst degration dye under visibe light and reudtion layer of electrochromic.
The orthrhombic V2O5 structue obtained that the powders annealed at 300oC for 1h. The smallest particle sizes (2~3μm) obtained by annealed at 400oC for 1h. The Nd doping V2O5 powders were using different temperature calcination, and produced to NdVO4 structure by XRD confirmation. The results the best photocataltic degration dye 67%。

摘要 i
Abstract ii
誌謝 i
目錄 i
圖目錄 iii
表目錄 vi
第一章 緒論 1
1.1 前言 1
1.2 研究動機 2
第二章 文獻回顧 5
2.1 粉末製備的方法 5
2.2 釹摻雜的五氧化二釩 6
2.3 光觸媒 7
2.4 電致變色 8
第三章 實驗方法與步驟 12
3.1 實驗藥品 12
3.2 五氧化二釩粉末之製備 14
3.3 釹摻雜五氧化二釩粉末之製備 16
3.4 光觸媒實驗 18
3.4.1 檢量線製作 18
3.4.2 光催化實驗 19
3.5 電致變色實驗 22
3.6 物性分析 25
第四章 實驗結果與討論 28
4.1 五氧化二釩粉末 28
4.1.1 五氧化二釩粉末的形成 28
4.1.2 煆燒溫度對形貌的影響 30
4.1.3 五氧化二釩粉末的結構和特點 33
4.2摻雜不同比例釹摻雜對沈澱物粉末之影響 37
4.3 粉末應用在光觸媒對染料降解之影響 45
4.4 電致變色之影響 49
第五章 結論 54
參考文獻 55

[1] 原晨光，還原五氧化二釩製備釩的低價氧化物，浙江大學，碩士論文，2005。
[2] L. Aquino-Meneses, R. Lozada-Morales, P. del Angel-Vicente , J. C. Percino-Picazo, O. Zelaya-Angel , M. Becerril, J. Carmona-Rodriguez , F. Rodriguez-Melgarejo, S. Jime´nez-Sandoval, Photoluminescence in Nd-doped V2O5,Journal of Materials Science, 2014, 49, 2298–2302.
[3] 吳佳霖，曾世賢，陳開煌，鄭建民，探討不同氧氣濃度於五氧化二釩薄膜在非揮發性變阻式記憶體元件之應用，南台科技大學，2009。
[4] 周竹君，應用釩氧化物光觸媒產氫之研究，國立臺北科技大學，碩士論文，2009。
[5] H. Fu, X. Jiang, X. Yang, A. Yu, D. Su, G. Wang, J. Nanopart, Res, 2011,14 , 871–885.
[6] Y. Chen, H. Xu, H.X. Feng, Mater. Res. Innov. 12 (2008) 78–80.
[7] Cao, A. M.; Hu, J. S.; Liang, H.P.; Wang, L. J. Angew. Chem., Int. Ed. 2005, 44, 4391.
[8] Zhou X W, Cui C J, Wu G M, et al. A novel and facile way to
synthesize vanadium pentoxide nanospike as cathode materials for
high performance lithium ion batteries [J]. Journal of Power Sources, 2013, 238 ( 15 ) : 95 - 102.
[9] P. Ragupathy, S. Shivakumara, H.N. Vasan, N. Munichandraiah, Preparation of Nanostrip V2O5 by the Polyol Method and Its Electrochemical Characterization as Cathode Material for Rechargeable Lithium Batteries, J. Phys. Chem., 2008, C (112) , 16700–16707.
[10] 陳康祺，五氧化二釩/鉑核殼奈米線之製備與特性研究，中國文化大學，碩士論文，2013。
[11] 邱聖堯，探討聚乙烯吡咯烷酮與醇類單體合成氧化鉬粉末之研究，國立聯合大學，碩士論文，2014。
[12] 王士庭，可見光應答氮氧化鈦光觸媒之材料特性與光催化活性探討，大同大學，碩士論文，2009。
[13] Beke S, A review of the growth of V2O5 films from 1885 to 2010,Thin Sol Films, 2011, 519, 1761–1771.
[14] Iwanaga S, Marciniak M, Darling RB, Ohuchi FS, Thermopowerand electrical conductivity of sodium-doped V2O5 thinfilms, J Appl Phys, 2007, 101(123709), 1–8 .
[15] AklAlaa A, Crystallization and electrical properties ofV2O5 thin films prepared by RF sputtering, App Surf Sci, 2007, 253,7094–7099.
[16] Yu DM, Zhang ST, Liu DW, Zhou XY, Xie SH, Zhang QF, Liu YY, Cao GZ, Effect of manganese doping on Li-ion intercalation properties of V2O5 films, J Mater Chem, 2007, 20, 10841–10846.
[17] Giorgetti M, Berrettoni M , Doped V2O5-based cathode materials: wheredows the doping metal go? An X-ray absorption spectroscopy study, Chem Mater, 2007, 19, 5991–6000.
[18] Zhan SY, Wang CZ, Nikolowski K, Ehrenberg H, Chen G, Wei YJ , Electrochemical properties of Cr doped V2O5 between 3.8 and 2.0 V, Sol State Ionics, 2009, 180, 1198–1203.
[19] Kryukova GN, Zenkovets GA, Pfa¨nder N, Su DS, Schlo¨gl R,Synthesis and characterization of the titanium doped nanostructural V2O5, Mater SciEng, 2001, A 343, 8–12.
[20] Kim H-K, Ok Y-W, Seong T-Y, Jeon EJ, Cho W i, Yoon YS , Microstructures and electrochemical properties of Ptdoped amorphous V2O5 cathode films for thin film microbatteries, J VacSci Tech , 2001, A 19(5), 2549–2553.
[21] D. Zhang, Synergetic effects of Cu2O photocatalyst with titania and enhanced photoactivity under visible irradiation, ActaChimicaSlovaca, 2013, 6(1) , 141-149.
[22] M. Zhang, J. Wu, D. Lu, J. Yang, Enhanced Visible Light Photocatalytic Activity for TiO2 Nanotube Array Films by Codoping with Tungsten and Nitrogen, International Journal of Photoenergy, 2013, 471674.
[23] 林文崇、鄭名翔、王婷玉、曾俊傑、陳裕傑，提升TiO2 光觸媒在可見光的催化活性，崑山科技大學，2012。
[24] 張仕正，在二氧化鈦上進行Salicylic acid 可見光光催化反應的研究, 國立中央大學，碩士論文，2003。
[25] 蘇俊鐘，光觸媒，NCHC 奈米科學研究小組，2003。
[26] 王士庭，可見光應答氮氧化鈦光觸媒之材料特性與光催化活性探討，大同大學，碩士論文，2009。
[27] 黃鴻泰，以溶膠-凝膠法製備WO3/V2O5 電致色變玻璃，逢甲大學，碩士論文，2006。
[28] 賈春陽，基于V2O5 的電致色變薄膜及柔性大面積電致色變器件研究，成都電子科技大學，碩士論文，2015。
[29] Y. Wei, M. Li, J. Zheng, et al. Structurl characterization and optical properties of V2O5 films prepared via ultrasonic spraying[J]. Thin Solid Films, 2013, 534, 446-451.
[30] 許朝勝，詹志潔，電致色變元件中不可或缺的橋梁-電解質，逢甲大學，化工技術，2007，54(2)，35-41。
[31] 劉展志，溶膠−凝膠法製備電致色變三氧化鉬薄膜，正修科技大學，碩士論文，2008。
[32] Y.Q.Wang, Z.C.Li, X.Sheng, Z.J.Zhang, J.Chem.Phys., 2007, 126, 164701-164703.