本文主要目地在探討在不同半徑球形刀具順銑與逆銑碳鋼曲面加工的粗糙度與幾何精度之影響。刀具選用球形R4mm、R3mm、R2mm銑刀、調整不同主軸轉速與進給率加減速來加工，觀察工件幾何曲面輪廓和粗糙度表面之狀況。
實驗結果顯示，使用較大半徑的球形R4mm端銑刀，在順銑削下且銑削間隔愈小，所得曲面工件表面粗糙度相對較佳於R3mm與 R2mm者，但曲面幾何輪廓精度相對較差。順銑削時所得工件表面粗糙度比逆銑削者佳。另外，在曲面轉折圓弧處降低主軸轉速與進給率銑削，可改善工件表面粗糙度。相對地，使用較小半徑R2mm球形端銑刀在順銑削下，所得工件表面粗糙度相對較差，但曲面幾何輪廓精度相對較高，其原因可能是刀具半徑較小，顫振較大，使表面粗糙度上升，但幾何輪廓精度較高，原因是減少曲面轉折圓弧處產生過切之故。

The main purpose of this paper was to investigate the effect of the down milling and up milling of carbon steel for the different radius of ball end mills on the roughness and geometric finish of the curved surface. The ball end mills with R4, R3 and R2 mm, the different spindle speed and feed rate or reducing spindle speed and feed rate were selected to study the roughness and geometric finish of curved surface.
The experiment results showed that using ball end mills of R4 mm under down milling of the curved surface and lower cross feed can obtain a relatively better workpiece roughness than those of R3 and R2 mm, but a poorer geometric finish. The workpiece surface roughness obtained for down milling was better than that of up milling. Besides, at inflection arcs of curved surface reducing spindle speed and feed rate during milling can improve the workpiece roughness. Relatively, using a smaller radius of ball end mills under down milling can cause a poorer curved roughness, but a better curved surface geometric finish. The reason for this is that the tool of smaller radius produces a larger chatter during milling, causing a poorer roughness. But the better curved geometric finish is attributed to reducing an overcut action at inflection arcs of curved surface.

致 謝
摘 要
ABSTRACT
目 錄
表 錄
圖 錄
第一章 緒 論
1.1前言
1.2文獻回顧
1.3 研究目的
1.4 本文內容
第二章 理論基礎
2.1切削力[16]
2.2逆銑與順銑
2.3 切削顫振[6 ,15]
2.4 表面粗糙度[15]
第三章 實驗規劃程序
3.1實驗
3.1-1加工材質
3.1-2加工條件
3.2實驗步驟及方法
3.3銑削路徑規劃
3.3-1 MASTERCAM軟體
3.3-2減速省時高效加工
3.4非接觸式光學掃描量測系統(ATOS)
3.5分析儀器及設備
第四章 實驗結果與討論
4.1工件表面粗糙
4.2工件轉折區域粗糙度比較
4.3表面粗糙度圖
4-4工件曲面精度
第五章 結論
參考文獻
附 件

[1] 羅明哲，小波轉換於轉子故障與切削颤振偵測之應用，中原大學機械工程研究所碩士論文，2001。
[2] 鄭嘉敏、巫聰獻，CNC工具機操作之數位學習研究，高鳳技術學院，2006。
[3] A.E. Hossein, Z. Yahya, “High-speed end-milling of AISI 304 stainless steels using new geometrically developed carbide inserts,” Journal of Materials Processing Technology, Vol. 162–163, pp.596–602, 2005.
[4] K.K. Kima, M.C. Kanga, J.S. Kima, Y.H. Junga, N.K. Kimb, “A study on the precision machinability of ball end milling by cutting speed optimization,” Journal of Materials Processing Technology, Vol.130–131, pp. 357 –362, 2002.
[5] Y. Su, N. He, L. Li, A. Iqbal, M.H. Xiao, S. Xu, B.G. Qiu, “Refrigerated cooling air cutting of difficult-to-cut materials,” International Journal of Machine Tools & Manufacture, Vol.47, pp.927–933, 2007.
[6] H.Z. Li, H. Zeng, X.Q. Chen, “An experimental study of tool wear and cutting force variation in the end milling of Inconel 718 with coated carbide inserts,” Journal of Materials Processing Technology, Vol. 180, pp. 296-304, 2006.

[7] 黃增煇，鋼材銑削性質評估指標之研究，國立成功大學機械工程研究所碩士論文，2003。
[8] 陳栖杰，CNC加工輪廓誤差之分析與補償，逢甲大學機械工程研究所碩士論文，2004。
[9] 王雪娥、何應勤，以田口法規劃曲面銑削之研究，第五屆精密製造學術研討會論文，2006。
[10] 郭銘修，銑削條件與刀具幾何對比銑削係數影響之研究，國立成功大學機械工程研究所碩士論文，2006。
[11] 李昭佐，端銑刀之傾角、螺旋角與鍍膜對銑削硬鋼工件表面粗糙度之影響，華梵大學機電工程研究所碩士論文，2007。
[12] 林鴻熊，端銑刀銑削SKD11硬鋼之刀具磨耗研究，華梵大學機電工程研究所碩士論文，2008。
[13] 胡昌霞，多軸加工誤差控制及刀具軸向設計，國立中央大學機械工程研究所碩士論文，2001。
[14] 許文通，17-4PH不銹鋼被削性之研究，國立中央大學機械工程研究所碩士論文，2006。
[15] 唐文聰編譯，精密機械加工原理，全華科技圖書股份有限公司，2004。
[16] 李均澤編著，切削刀具學，新文京開發出版有限公司，2006。
[17] 鐘華玉、陳添鎮編著，Mastercam 2D繪圖與加工教學手冊，全華科技圖書股份有限公司，2007。
[18] 楊榮顯編著，機械材料，逢甲書局公司，1986。
[19] 徐明監編著，最新切削加工技術，復漢出版社，2000。
[20] 傅光華校閱余永平，鄭正德、劉見成編譯，機械加工法(下)，高立圖書有限公司，1993。