DP6-PPV－ poly（2,3-diphenyl-5-hexyl-1,4-phenylenevinylene） 是個發藍綠光的高分子且具有高螢光效率，MEH-PPV－poly[2-methoxy-5-(2’ethylhexyloxy)-1,4- phenylenevinylene]是發橘紅光的高分子，且對一般做旋轉塗佈的溶劑皆具有相當的溶解度。我們利用Gilch route的方法合成不同比例的共聚物，並且加入抑制劑來改善高分子共聚物的分子量分佈，減低凝膠化的機率，以及利用不同比例單體的聚合得到不同光色且具有不錯溶解度的高分子共聚物。
我們以聚合所得到的高分子共聚物當成發光層，以ITO玻璃基板為陽極，鎂與銀為陰極，製作單層高分子發光二極體，因為高分子共聚物具有不錯的溶解度，所以有利於我們元件的製作，因此我們可以簡單的利用合成的方法得到不同光色的高分子，進而製作成不同光色的高分子發光二極體元件。

We present synthesis and characterization of copolymers. In this study, copolymers of poly (2,3-diphenyl-5-hexyl-1,4-phenylenevinylene)(DP6-PPV) and poly [2-methoxy- 5-(2’ethylhexyloxy)-1,4-phenylenevinylene] (MEH-PPV) have been synthesized via a modified Gilch route involving the use of an acidic additive such as 4-tert-butylbenzyl chloride. As a result of this modified polymerization route, gelation can be minimized and the resulting copolymers were well soluble in common organic solvent, such as THF, toluene and chloroform etc. Blue-green to orange-red emission of copolymers was achieved by the different feeding ratio of two monomers.

目 次
中文摘要
英文摘要
誌謝
目次
表目錄
圖目錄
第一章 緒論
1.1研究動機
1.2高分子發光二極體發光原理及基本構造
1.3高分子發光材料
1.3.1主鏈型高分子發光材料
1.3.2側鏈型高分子發光料
第二章 實驗部分
2.1實驗藥品
2.2物性及分析儀器
2.3高分子發光材料合成方法
2.3.1 DP6-PPV合成方法
2.3.2 MEH-PPV合成方法
2.3.3 MEH-PPV與DP6-PPV高分子共聚物合成方法
2.3.4 MCH-PPV合成方法
2.4高分子聚合反應機制
2.5高分子發光二極體元件製作
2.5.1 高分子溶液配製
2.5.2 ITO-玻璃基版的蝕刻與清洗
2.5.3 高分子塗佈成膜
2.5.4 蒸鍍(thermal evaporation)陰極
2.5.5 高分子發光元件量測
第三章 結果與討論
3.1DP6-PPV高分子材料特性分析
3.1.1氫核磁共振光譜圖(1H-NMR)
3.1.2分子量分佈光譜圖(GPC)
3.1.3紫外-可見光吸收光譜圖(UV-Vis absorption)
3.2MEH-PPV高分子材料特性分析
3.2.1氫核磁共振光譜圖(1H-NMR)
3.2.2分子量分佈光譜圖(GPC)
3.2.3紫外-可見光吸收光譜圖(UV-Vis absorption)
3.3DP6-PPV與MEH-PPV高分子共聚物材料特性分析
3.3.1氫核磁共振光譜圖(1H-NMR)
3.3.2分子量分佈光譜圖(GPC)
3.3.3紫外-可見光吸收光譜圖(UV-Vis absorption)
3.4MCH-PPV高分子材料特性分析
3.4.1氫核磁共振光譜圖(1H-NMR)
3.4.2分子量分佈光譜圖(GPC)
3.4.3紫外-可見光吸收光譜圖(UV-Vis absorption)
3.5高分子發光二極體元件特性分析
3.5.1光致發光(PL)與電致發光(EL)光譜分析
3.5.2電流密度(I)-電壓(V)圖譜分析
3.6結果整理
第四章 結 論
參考文獻
附錄

【1】J. H. Burroughes, D. D. C. Bradley, A. R. Brown, R. N. Marks, K. Mackay, R. H. Friend, P. L. Burns and A. B. Holmes, Nature, 1990, 347, 539.
【2】M. Pope, H. P. Kallmann and P. Magnante, J. Chem. Phys., 1963, 38,2042.
【3】C. W. Tang and S. A. Vanslyke, Appl. Phys. Lett., 1987, 51, 913.
【4】G. Gustafsson, Y. Cao, G. M. Treacy, F. Klavetter, N. Colaneri and A. J. Heeger, Nature, 1992, 357, 477.
【5】B. R. Hsieh, Y. Yu, E. W. Forsythe, G. M. Schaaf and W. A. Feld, J. Am. Chem. Soc., 1998, 120, 231.
【6】A. R. Brown, D. D. C. Bradley, J. H. Burroughes, R. H. Friend, N. C. Greenham,
P. L. Burn, A. B. Holmes and A. Kraft, Appl. Phys. Lett., 1992, 61, 2793.
【7】J. Salbeck, Ber. Bunsenges. Phys. Chem., 1996, 100, 1666.
【8】N. C. Greenham, S. C. Moratti, D. D. C. Bradley, R. H. Friend and A. B. Holmes, Nature, 1993, 365, 628.
【9】D. H. Hwang, S. T. Kim, A. B. Holmes and R. H. Friend, H. K. Shim and S. C. Moratti, Synth. Met., 1997, 84, 615.
【10】C. Zhang, H. von Seggern, K. Pakbaz, B. Kraabel, H. W. Schmidt and A. J. Heeger, Synth. Met., 1994, 62, 35.
【11】Y. Ohmori, K. Uchida, K. Muro and K. Yoshino, Jpn. J. Appl. Phys., 28, p.1433(1991)
【12】Q. Pei, Y. Yang, J. Am. Chem. Soc., 1996, 118, 7416.
【13】G. Grem, G. Leditzky, B. Ullrich and G. Leising, Synth. Met., 1992, 51, 383.
【14】Y. Yang, Q. Pei and A. J. Heeger, J. Appl. Phys., 1996, 79, 934.
【15】Y. Ohmori, M. Uchida, K. Muro, and K. Yoshino, Jpn. J. Appl. Phys., 1991, 30, 1938.
【16】Y. Ohmori, M. Uchida, K. Muro, and K. Yoshino, Solid State Commun., 1991, 80, 605.
【17】D. Braun, G. Gustafsson, D. McBranch and A. J. Heeger, J. Appl. Phys., 1992, 72, 564.
【18】M. Uchida, Y. Ohmori, C. Morishima and K. Yoshino, Synth. Met., 1993, 57, 4168.
【19】N. C. Greenham, A. R. Brown, D. D. C. Bradley and R. Friend, Synth. Met., 1993, 57, 4134.
【20】Y, Xiao, W. L. Yu, J. Pei, Z. Chen, W. Huang and A. J. Heeger, Synth. Met., 1999, 106, 165.
【21】D. M. Johansson, G. Srdanov, G. Yu, M. Theander, O. Inganäs and M. R. Andersson, Macromolecules, 2000, 33, 2525.
【22】L. S. Park, Y. S. Han, S. D. Kim and D. U. Kim, Synth. Met., 2001, 117, 237.
【23】D. J. Choo, A. Talaie, Y. K. Lee, J. Jang, S. H. Park, G. Huh, K. H. Yoo and J. Y. Lee, Thin Solid Films, 2000, 363, 37.
【24】F. Cacialli, X. C. Li, R. H. Friend, S. C. Moratti, A. B. Holme, Synth. Met., 1995, 75, 161.
【25】H. G. Gilch, and W. L. Wheelweight, J. Polym. Sci., Part A : Polym. Chem., 1966, 4, 1337.