本研究探討不同陽離子型光起始劑、組成與紫外光照射時間等對alicyclic diepoxy樹脂硬化後之光穿透率之影響。期間利用傅立葉轉換紅外線光譜儀(FTIR)分析其轉化率尋找加工硬化條件，藉由紫外光/可見光譜儀量測穿透率，並以熱分析儀：DSC與TGA測試其熱性質異。結果發現使用5wt% UVI 6992之起始劑，硬化後薄膜光穿透率範圍較廣，於波長470nm時，穿透率可達90%以上，添加1.5wt%之抗氧化劑對其光穿透率範圍並無顯著影響。另一方面，使用UVI 6976起始劑硬化後之薄膜，波長需達670nm以上，穿透率方可達80%，但是可以添加抗氧化劑提高其透明度，值得再加以詳細研究探討其中原因。本研究部分成果可以作為光電元件高透明度封裝材料之基本配方。

Alicyclic diepoxy resin was cured with different initiators, UVI 6992 and 6976, under UV radiation. The conversion and thermal properties of the cured films were investigated by a FTIR, DSC, and TGA. The transmission of the epoxy film was measured by a UV/VIS spectrometer. It was found that when the epoxy resin cured with the initiator, UVI 6992, the transmission is larger than 90% after wave length of 470 nm, and it is not changed apparently with addition of an antioxidant. On the other hand, with UVI 6976, the transmission of the cured film is lower, which is about 80% after wave length of 670nm, but increases by adding the antioxidant. The cause is worthy of further study. The results can be extended to develop the encapsulate materials of photo-electro devices.

摘要…………………………………………………i
Abstract…………………………….…………..ii
致謝……………………………………………..iii
目錄…………………………....….……………iv
表目錄…………………..………………………vii
圖目錄……………………………………….……ix
第一章 緒論…………………………………….. 1
1.1 前言……….………………………………1
1.2 光硬化樹脂之簡介…………………….…2
1.3 光硬化樹脂的特性……………………….3
1.4 研究動機………………………….………6
第二章 文獻回顧………………………….….. .7
2.1 UV光源的定義與應用………….…………7
2.1.1 UV光源的定義………………………7
2.1.2 UV光的應用…….………………….9
2.1.3 UV光源對人體之危害及安全問題..9
2.2 光硬化樹脂之起源……….…….………10
2.3 光硬化樹脂之種類………………………11
2.3.1 乙烯基類反應性樹脂……….……11
2.1.2 非乙烯基類反應性樹脂………….12
2.4 光硬化樹脂之組成………………………17
2.4.1 活性寡聚體……………………….18
2.4.2 反應性稀釋單體………………….23
2.4.3 光起始劑………………………….26
2.4.4 光增感劑………………….………27
2.4.5 添加劑…………………………….28
2.5 抗氧化劑…..……………………………31
2.6 影響應化之因素…………………………33
2.7 光學與色彩學原理………………………36
2.7.1 光和光源……………………….…36
2.7.2 色座標與色度圖...............36
第三章 實驗方法…………………….……….. 48
3.1 實驗簡介…………………….….………48
3.2實驗藥品……………………….…………48
3.1.1 Monomer之藥品………….….……49
3.1.2 Photoinitiator之藥品…….……50
3.1.3 添加劑之藥品……….……………50
3.3實驗設備及器材………….………………50
3.4實驗流程及方式……………………….…53
第四章 結果與討論…………………… ....….54
4.1不同光起始劑濃度對反應之影響……… 54
4.2不同光起始劑濃度對穿透率之影響….…60
4.3不同抗氧化劑濃度對穿透率之影響…….69
4.4不同抗氧化劑濃度對色差之影響….……79
4.5熱物性測試……..………………….……83
4.5.1 光起始劑熱裂解測試…………….83
4.5.2 抗氧化劑試片熱裂解測試……...83
4.5.3 光起始劑DSC反應程度測試……..84
4.5.4 光起始劑熱膨脹測試………….…85
4.5.5 光起始劑光反應測試……….……86
4.6 硬度測試………………………..………87
第五章 結論與建議……………………….……103
第六章 參考文獻……………………….………104
附錄 .………….…………….……...……….110

期刊
1.林和玫，陽離子型UV硬化技術與應用，光電電子元件及製程用感光材料技術專題，2005.03 NO.21，第41-47頁，2005
2.林瑜平，精密塗佈製程之光-紫外線硬化技術之應用，工業材料雜誌，第219期，2005，第102-108頁
3.謝添壽、陳曼玲等，ODF封膠材料技術，工業材料雜誌，第214期，2005，第176-181。
4.張上鎮，「紫外光硬化塗料與塗裝(4)」，塗料與塗裝技術，第六十一期，2005， 第87-90頁
5.D. K. Chattopadhyay, Siva Sankar Panda, K.V.S.N. Raju , "Thermal and mechanical properties of epoxy acrylate/methacrylates UV cured coatings, "Progress in Organic Coatings 54, 2004, pp.10
6.Xuesong Jiang,Hongjie Xu and Jie Yin , "Polymeric amine bearing side-chain thioxanthone as a novel photoinitiator for photopolymerization," Polymer., vol. 45, 2004, pp.139.
7.Dae Su , Woo Hyun Sec , "Ultraviolet-Curing Behavior and Mechanical Properties of a Polyester Acrylate Resin , " J. Appl. Polym. Sci, vol. 92, 2004, pp.3921
8.劉建良，「UV Curing發展簡介及應用」，化工科技與商情，第四十一期，2003， 第1-4頁
9.Duygu Avci,Jennifer Nobles and Lon J. mathias, "Synthesis photopolymerization kinetics of new flexible diacrylate and dimethacrylate crosslinkers based on C18 diacid," Polymer, vol. 44, no. 1, 2003, pp.964-967.
10.Huiguang Kou,Anila Asif and WenFang Shi , "Photopolymerization kinetics of Hyperbranched Acrylated Aromatic Polyester," J. of Appl. Polym.Sci., vol. 89, 2003, pp.1503.
11.陳奇毅，「UV Curable樹脂於不同波長之反應探討」，第十八屆纖維紡織科技研討會論文集，桃園，2002，第CP008頁
12.劉廣定，「化學與化工的永續發展」，科技與人文對話，台大共同教育委員會， 第103-109頁，2002
13.張上鎮，「紫外光硬化塗料與塗裝(3)」，塗料與塗裝技術，第三期，2002，第9-10頁
14.宋博厚、林羿刪，黏土補強水性PU樹脂探討，輔仁大學研究所， NSC91-2216-E-030-002，2002
15.Timothy F. Scott,Wayne D. Cook and John S. Forsythe , "Photo-DSC cure kinetics of vinyl ester resins.Ⅰ.Influence of temperature," Polymer., vol. 43, 2002, pp.5839-5841.
16.張上鎮，「紫外光硬化塗料與塗裝(1)」，塗料與塗裝技術，第二十一期，2001， 第22-30頁
17.余福熙，「如何選擇及使用紫外線/可視光硬化型接著劑」，化工科技與商情， 第十七期，2001，第9-12頁
18.De Lin,Huiguang Kou,Wen-Fang Shi,Hui-Ya Yuan and Yong-Lie Chen, "Photopolymerization of Hyperbranched Aliphatic Acrylated Poly(amide ester).Ⅱ.Photopolymerization Kinetics," J. of Appl. Polym.Sci., vol. 82, 2001, pp.1640.
19.Huanyu Wei,Huiguang Kou,WenFang Shi,Hui-Ya Yuan and Yong-Lie Chen, "Photopolymerization kinetics of dendritic poly(ether-amide)s," Polymer., vol. 42, 2001, pp.6744.
20.L. Lecamp,P. Lebaudy,B. Youssef and C. Bunel , "Influence of UV radiation wavelength on conversion and temperature distribution profiles within dimethacrylate thick material during photopolymerization," Polymer., vol. 42, 2001, pp.8544.
21.Tom Scherzer and Helmut Langguth , "The effect of temperature on the induction period in the photoinitiated polymerization of tripropylene glycol diacrylate," NIMB., vol. 185, 2001, pp.278.
22.Susana B. Grassino,Miriam C. Strumia,Joel Couve and Marc J. M. Abadie, "Photoactive films obtained from methacrylo-urethanes tannic acid-based wuth potential usage as coating materials：analytic and kinetic studies," progress in Organic Coating., vol. 37, 1999, pp.45.
23.L. Lecamp,B. Youssef,C. Bunel and P. Lebaudy , "Photoinitiated polymerization of a dimethacrylate oligomer：1.Influence of photoinitiator concentration, temperature and light intensity ," Polymer., vol. 38, 1997, pp.6091.
24.C. Allan Guymon and Christopher N. Bowman, "Polymerization Behavior and Kinetics during the Gormation of Polymer-Stabilized Ferroelectric Liquid Crystals," Macromolecules., vol. 30, 1997, pp.1596.75
25.P. F. Bunyan and A. V. Cunliffe , " Microcalorimetric determination of the cure reaction in some fluorinated polyether rubbers," Thermochimica acta, vol. 276, 1996, pp.134
26.E. W. Nelson,J. L. Jacobs and A. B. Scranton , "Photo-differential Scanning Calorimetry studies of cationic polymerizations of divinyl ethers," Polymer., vol. 36, 1995, pp.4653.
27.JosÉ M. kenny, "Determination of Autocatalytic Kinetic Model Parameters Describing Thermoset Cure," J. of Appl. Polym.Sci., vol. 51, 1994, pp.761-763.
28.郭永言，「紫外線之測量」，核研月刊6，第101-105頁，1993
29.吳丁凱，光硬化型樹脂的發展動向，專題調查報告，工業技術研究院化學工 業研究所，新竹，1987
30.A. Moroni , J. Mijovic , E. M. Pearce and C. C. Foun , " Cure Kinetics of Epoxy Resins and Aromatic Diamines," J. Appl. Polym. Sci, vol. 32, 1986, pp.3761
31.陳暉，「UV硬化技術入門(一)」，高分子工業，第三十四期，1985，第65頁
32.James V. Crivello, Clifton Park, N.Y., "Curable epoxy compositions containing aromatic onium salts and hydroxy compounds, "United States Patent, Nov 27, 1979, 4175972
33.James V. Crivello, Clifton Park, N.Y., "Curable compositions, "United States Patent, Nov 27, 1979, 4175973
34.Y. S. Pusatciolu, A. L. Fricke and J. C. Hassler, " Heats of Reaction and Kinetics of a Thermoset Polyester," J. Appl. Polym. Sci, vol. 24, 1979, pp.937
35.James V. Crivello, Elnora, N.Y., "Photocurable epoxy compositions containing group va onium salts, "United States Patent, Jan.17, 1978, 4069055
36.James V. Crivello, Elnora, N.Y., "Photocurable compositions containing group via aromatic onium salts, "United States Patent, Nov.15, 1977, 4058401
37.K. Dusek and M. Bleha , " Curing of Epoxide Resins :Model Reaction of Curing with Amine ," J. Polym. Sci,Polym Chem Ed., vol. 15, 1977, pp.2393.
38.R.B.Prime , " Differential Scanning Calorimeter of the Epoxy Cure Reaction ," Polymer Eng. Sci., vol. 13, 1973, pp.365.
39.Horie , " Calorimetric Investigation of Polymerization Reactions. III. Curing Reaction of Epoxides with Amines," J. Polym. Sci, A-1,8, 1970, pp.1357

論文
40.吳聖安，矽氧烷改質奈米級二氧化矽之合成及做為UV塗料添加劑之研究，碩士論文，嘉義大學環境暨自然資源研究所，嘉義，2006
41.郭政翰，陽離子型環氧樹脂之供應化動力學分析與機械性質探討，碩士論文， 台北科技大學有機高分子研究所，台北，2005
42.何志松，紫外光硬化壓克力樹脂之研究，碩士論文，東海大學化學工程研究所，台中，2005
43.蘇宇傑，光/熱硬化型環氧丙烯酸酯樹脂之合成及其性質，碩士論文，淡江大學化學工程與材料工程學系碩士班，台北，2005
44.黃錫裕，UV Curable PU之光硬化動力學分析，碩士論文，台北科技大學有機 高分子研究所，台北，2004
45.游恩華，紫外線成型技術探討與應用，碩士論文，東華大學材料科學與工程 研究所，花蓮，2004
46.郭義鵬，藍色系壓克力樹脂光硬化行為之摻合效應及光學性能之研究，碩士論文，台灣科技大學高分子工程系，台北，2004
47.蔡銘翰，薄膜電晶體液晶顯示器感光性高分子材料之研究，碩士論文，台北科技大學有機高分子研究所，台北，2004
48.許家銘，彩色濾光片之二相系之光硬化樹脂混掺硬化行為探討，碩士論文， 台灣科技大學高分子工程研究所，台北，2003
49.林子孟，紫外光硬化型樹脂之光硬化動力學及熱物性研究，碩士論文，臺北 科技大學化學工程系研究所，台北，2003
50.曾士恭，紫外光可硬化型聚胺酯壓克力樹脂之研究，碩士論文，臺灣大學化學工程研究所，台北，2003
51.陳奇毅，UV Curable PU樹脂於不同波長之反應性探討，碩士論文，台北科技 大學有機高分子研究所，台北，2002
52.傅亞卿，高折射率環氧樹脂之合成及其物性研究，碩士論文，台灣大學材料 與工程學研究所，台北，2001
53.郭耀凱，張頁式PVC平版印刷UV光源最佳設置模式之研究，碩士論文，中 國文化大學印刷傳播研究所，台北，2001
54.丁凡隼，具附加型官能基之光硬化樹脂的合成及其成膜特性，碩士論文，大同大學化學工程研究所，台北，2001
55.劉恆瑜，DPC與RPT分析壓克力聚酯系樹脂光硬化行為及物性之研究，碩士論文，台灣科技大學纖維及高分子工程研究所，台北，2000
56.彭志成，紫外光可硬化之聚胺酯，碩士論文，臺灣大學化學工程研究所，台 北，1998
57.許富蘭，紫外光硬化塗料之耐光性與耐候性之比較與改善，碩士論文，臺灣 大學森林學研究所，台北，1994
58.葉金泉，紫外線硬化環氧樹脂合成，碩士論文，成功大學化學工程研究所， 台南，1986