本研究嘗試著組裝一台可製作奈米粉末的設備，係藉由文獻和專利的收集，再經改良和設計，以電漿電弧為加熱源。使用電漿電弧為加熱源優點主要是功率大、可氣化各種金屬與陶瓷材料、同時能用於實驗室規模量產。最後分析由腔體內不同位置置放之鋁箔和Cold-trap所搜集之粉末，來評估本自行研製設備的穩定性及其優劣情況。
實驗結果顯示，所得到的TiO 微粒的平均粒徑大約20nm左右。觀察鋁箔所收集之粉末，得知粉末成長10~20倍（相對於Cold-trap收集之粉末而言）。鋁箔放置位置與粉末粒徑大小有關，放置離蒸發源越遠，粉末粒徑越大。每組上半部由於受輻射熱影響較大，所以粉末粒徑較大。本實驗系統製作之TiO2粉末以Rutile相所佔之比率較大，表示製作過程中，由於受輻射熱影響，已經發生相變化。與國外所製作之TiO2粉末比較，本實驗系統能製作比國外TiO2粉末粒徑還小10nm，表示本實驗設備具有相當的潛能。

A laboratory-made equipment was developed and fabricated in this study to produce nanopowder. According to the published papers and patents a new equipment is designed and tested in our department. This equipment uses plasma arc as a heating source. In this heating source, all of the metal and ceramics materials can be vaporized. This equipment is also effective, inexpensive and suitable to a laboratory scale. The collected powders from different positions in the aluminum foil and cold-trap of the chamber were analyzed using SEM and XRD. The characteristic and stability of this equipment was also evaluated.
The experiment result shows that the average particle diameter of TiO2 powder is about 20nm. The powder obtained from aluminum foil is 10~20 times the average particle diameter of that obtained from cold-trap. The size of the average particle diameter of powder is related to the position where powder obtained. The far from the vapor source, the larger the average particle diameter of powder. Due to more irradiation, powder with larger particle diameter can be obtained in the upper part of the chamber.
In this experimental system, the Rutile phase have more ratios in the powder of TiO2. This shows the powder have changed its phase during fabricating process because of the influence of irradiation heat. Compared with powder of TiO2 obtained from abroad, this experimental system can produce powder with a particle diameter of less than 10 nm. Therefore, this equipment have a good potential to a future study.

頁次
中文摘要 …………………………………………….…………… I
英文摘要 ………………………………………………………… II
誌 謝 ………………………………………………………… III
目 錄 ………………………………………………………… IV
表 目 錄 ………………………………………………………… VII
圖 目 錄 ………………………………………………………… VIII
第一章 序論…………….……………………………………… 1
1. 1 前言……….…………………………………………… 1
1. 2 研究動機與目的.……………………………………… 3
第二章 文獻回顧..……..………………………………………4
2. 1 奈米材料簡介……….…………………………………4
2.1.1 奈米材料.………………………………………………4
2.1.2 奈米材料之特性.………………………………………4
2.1.3 TiO2奈米粉末的特性與應用…………………………8
2.1.4 奈米材料的發展與應用…..…………………………9
2.1.5 奈米材料的分析………………..……………………13
2.1.6 奈米材料的製造技術………………..………………14
2. 2 氣凝合成法……..…..…….…..…………………15
2.2.1 氣凝生成過程………………………………………15
2.2.2 影響奈米粒子大小的因素…………………………15
2.2.3 生成煙的構造和不同區域的粒子尺寸……………17
2. 3 電漿電弧氣凝合成製造法……..…………………18
2.3.1 電漿電弧加熱原理…………………………………20
2.3.2 電漿電弧加熱系統………..…….…………………22
2.3.3 電漿電弧加熱製造流程……..…….………………23
第三章 成核原理與成長理論….……………………………26
3. 1 成核原理…………………………….………………26
3. 2 成核速度…..…………………………………….…28
3. 3 成長原理…..…………………………………….…29
3. 4 成長速度..……………………………….…………31
3. 5 單位體積中粒子間的碰撞頻率....…….…………31
第四章 實驗方法與步驟……….……………………………33
4. 1 實驗流程步驟………………………………………33
4. 2 專利的收集和創新…………………………………34
4.2.1 電漿電弧系統先前的設計...………………………34
4.2.2 創新的電漿電弧系統…..…………………………35
4. 3 設備組裝……………..……….……………………37
4.3.1 電源供應器….…………….…………………….…37
4.3.2 電將槍體……………….……….……………….…37
4.3.3 粉體收集系統……….………….……………….…37
4.3.4 給氣系統………………………..……………….…37
4.3.5 真空幫浦…………………….….……………….…37
4.3.6 腔體……………………………………..…………38
4. 4 設備測試…….……………….……………………40
4.4.1 製程參數設計……………………………..………40
4.4.2 通入氣體流量設計…………………………….……40
4.4.3 其他參數設計……………………………………….40
4.4.4 鋁箔置放位置設計……………....………………40
4.4.5 材料的選用與前處理…..………………….………42
4.4.6 奈米粉末製作步驟……..………………………….42
4.4.7 奈米粉末收集與保存………………………………43
4. 5 微結構分析…………………………….……………43
4.5.1 TEM 分析……………………………….……………43
4.5.2 SEM 分析….…………………………….……………44
4.5.3 XRD 分析………….…………….……………………44
4. 6 設備改善….………………..…………………………44
4. 7 設備完成………..….…………………………………46
第五章 結果與討論………………………………………………47
5. 1 晶粒大小分析……………..……………………………47
5. 2 粉末在Chamber中的粒徑分佈分析………………………50
5. 3 晶體結構分析……………………...……………………70
5. 4 與國外公司製造的TiO2 粉末比較………………...……72
第六章 結論與未來展望…………………………………….……75
6. 1 結論………..…………………………………………..…75
6. 2 未來展望……………………………….…………………76
參考文獻 ……………………………….……………………….……77
附錄一 U.S.專利 5,874,684之各部分零件的功能說明……………81
附錄二 國外公司製造的TiO2產品特性………………………………94

1. P. Cheyssac, R. Koofman, G. Mattei, P. G. Merli, A. Migliori and A. Stella, Superlattices and Microstructures, 17, (1995) 47.
2. G. Bertsch, Science, 277, (1997) 1619.
3. S. L. Lai, Phys. Rev. Lett, 77, (1996) 99.
4. T. S. Ahmadi, S. L. Logunov and M. A. El-Sayed, J. Phys. Chem, 100, (1996) 8053.
5. S. L. Logunov, T. S. Ahmadi, J. T. Khoury, R. L. Whetten and M. A. El-Sayed, J. Phys. Chem, 101, (1997) 3713﹒
6. S. S. Chang, C. W. Shih, C. D. Chen, W. C. Lai and C. R. C. Wang, Langmuir, 15, (l999) 701﹒
7. B. M. I. Van der Zande, M. R. Bohmer, L. G. J. Fokkink and C. Schonenberger, Langmuir, 16, (2000) 451.
8. R. Dagani, C&E, 23, (1992) 18.
9. J. Abellan, A. Arenas, R. Chicon and F. Reyes, Surface Science, 372, (1997) L315.
10. S. D. Brorson, J. G. Fujimoto and E. P. Ippen, Phys. Rev. Lett, 59, (1987) 1962﹒
11. K. Kalyanasundaram, E. Borgarello, D. Duonghong and M. Gratzel, Angew. Chem. Int. Ed. Engl, 20, (1981) 987.
12. 蘇品書，超微粒子材料技術，復漢出版社，台南，民國78年2月。
13. M. H. Teng, J. J. Host, J. H. Hwang, B. R. Elliott and et al , J.Mater.Res, 10, No. 2, (1995) 233.
14. 周長彬，蔡丕椿，郭央諶，銲接學，全華科技，民國88年11月。
15. L. Harris, D. Jeffries and B. M. Siegel, J. Appl. Phys, 19, (1948) 791.
16. R. Kubo, Japan J. of the Physical Society, 17, (1962) 975.
17. K. Kimoto, Y. Kamiya, M. Nonoyama and R. Uyeda , Japan J. Appl. Phys , Vol. 2, (1963) 702.
18. K. Kimoto and I. Nishida , Japan. J. Appl. Phys, Vol. 6, (1967) 1074.
19. R. Birringer and H. Glriter, in Encyclopaedia of Materials Science and Engineering, Suppl. 1, ed. R. W. Cahn, (1988) 339.
20. R. Mehrabian and et al, Nanostructure, DARPA Workshop, La Jalla, CA, July (1988).
21. Research Opportunities for Materials with Submicro-sized Microstructure, NMAB-454, Nation Academy Press.
22. Ultrafine Particle-science and Application, Japan Chemistry Society No.48, (1985).
23. X. Zhu, R. Birringer, U. Herr and H. Gleiter, Phys. Rev. B, 35, (1989) 9085.
24. F. H. Froes and C. Suryanarayana, JOM, June (1989) 12.
25. R. Birringer , Material Science and Engineering, A, 117, (1989) 33.
26. R. P. Andres, R. S. Arerback and et al, J. Mater. Res, 4, No.3, May/June, (1989) 704.
27. 賴宏仁，林景正，「奈米材料與技術專題」，工業材料153期，88年 9
月，94。
28. 周淑金，葉信宏，「光觸媒技術應用簡介」，工業材料，150期，88年6月，168。
29. 林景正，「奈米材料技術與發展趨勢」，電子月刊，第六卷第3期，89年 3月，206。
30. X. Zhu, Ph. D. Thesis, 1986, University of Saarburchen.
31. Q. Yitai, H. Yuan, W. Chengyun and C. Zuyao, Nanostructured Materials,1, (1992) 347.
32. E. Jorra, H. Franz, J. Peisl, G. Wallner, W. Petry, T. Houboled, R. Birringer and H. Gleiter, Phil. Mag. B, 60, (1989) 159.
33. T. Harbold, R. Birringer, B. Lengeler, U. Gonser and H. Gleiter , Phys. Lett. A, 135, (1989) 461.
34. U. Herr, J. Jing, R. Birringer, U. Gonser and H. Gleiter, Appl. Phys. Lett, 50 (1987) 472.
35. H. E. Schaefer and R. Wurschum, Phys. Lett. A, 119, (7), (1987) 370.
36. R. Wurschum, M. Scheytt and H. E. Schaeger, Phys. Stat. Sol. (a), 102, (1987) 119.
37. M. Arai, S. Hayshi and K. Yamamoto, Solid state Communications, 75, (7), (1990) 613.
38. R. Okada, Appl. phys. Lett, 58, (1991) 1662.
39. N. Wada, Japan J. Appl. Phys, 6, (1967) 553.
40. N. Wada, Japan J. Appl. Phys, 7, (1968) 1287.
41. F. H. Froes and C. Suryanarayana, JOM, June, (1989) 12.
42. S. Yatsuya, S. Kasukabe, and R. Uyeda, Jpn. J. Appl. Phys, 12, (1973) 1675.
43. S. Y. Chhou , P. R. Krauss and L. Kong, ibid, 79, (1996) 6101.
44. P. R. Krauss and S. Y. Chou, J.Vac.Sci.Technol. B13, (1995) 2850.
45. Y. Wang and N. Herron, J.Phys.Chem, 91, (1987) 257.
46. J. Gonzalo, C. N. Afonso and I. Madariaga, Apppl.Phys, 81, (1997) 951.
47. A. Henglein, J.Phys.Chem, 97, (1993) 5457.
48. V. Enustun and J. TurkevichJ, Am. Chem. Soc, 85, (1963) 3317.
49. J. L. Cain and D. E. Nikles, IEEE , 32, (1996) 4490.
50. H. H. Huang, F. Q. Yan, Y. M. Kek, C. H. Chew, G. Q. Xu, W. Ji, P. S. Oh and S. H. Tang, Langmuir, 13, (1997) 172.
51. Y. Yu, S. Chang, C. Lee and C. R. C. Wang, J. Phys. Chem. B, 101,34, (1997) 6661.
52. M. V. Seregina, L. M. Bronstein, O. A. Platonova, D. M. Chernyshov and P. M Valetsky, Chem. Mater, 9, (1997) 923.
53. S. J. Cho, S. M. Jung, Y. G. Shul and R. Ryoo, J. Phys. Chem, 96, (1992) 9922.
54. S. Mann, Nature, 365, (1993) 499.
55. 賴明雄，“超微粒貴金屬與其載體之界面研究”，大同工學院材料工程研究所碩士論文，民國80年。
56. 赤崎正則，賴耿陽，電漿工學的基礎，復文，台南市，民國75年。
57. 高正雄譯，工業調查會電子材料編集部編，電漿化學，復漢，台南市，民國80年。
58. 莊萬發，超微粒子理論應用，復漢出版社，台南，民國88年6月。
59. 超微粒子-科學應用，日本化學會，化學總說NO.48，23，1985。
60. B. Xia, H. Huang and Y. Xie, Materials Science and Engineering, B57, (1999) 150.