混凝土結構物為確保使用生命週期，必須從配比設計、施工過程及維護時，均需將混凝土耐久性問題納入考量。增加混凝土結構物抵抗化學侵蝕、磨損、風化等其他可能對其造成的破壞力，以提昇混凝土使用生命週期。
本文主要內容為針對混凝土結構物提昇耐久性必須考量項目予以說明，含括混凝土受力學侵襲耐久性、混凝土受物理侵襲耐久性，再予探討添加單一卜作嵐材料與同時添加二種卜作嵐材料（飛灰、爐石粉）用量取代水泥量。比較在不同卜作嵐材料於波特蘭Ⅰ、Ⅱ型水泥混凝土之耐久性質，如抗壓強度、吸水率、電阻係數與氣體滲透試驗等，以供參考。

The concrete structure in order to ensure the use of life-cycle. From the mixed proportion design, construction process and maintenance have to consider the problem for the durability of concrete. The concrete structure increase resistance to chemical attack, abrasion-erosion, weathering and other destructive forces. The use of concrete in order to enhance the life cycle.
The purpose of this study is to enhance the durability of concrete structure must be considered the item and statement. Including the durability of concrete by the fracture mechanics invasion, physical invasion and discuss with a single pozzolanic materials and at the same time add two pozzolanic materials (Fly ash and/or furnace slag) to replace cement. Comparing different pozzolanic materials in the durability feature of portland cement type I and type II concrete. Lab tests include compressive strength test, absorption test, resistivity test and gas penetration test.

摘 要 ……………………………………………………………………Ⅰ
Abstract …………………………………………………………………...Ⅱ
誌 謝 ……………………………………………………………………Ⅲ
目 錄 ……………………………………………………………………Ⅳ
表目錄 ……………………………………………………………………Ⅵ
圖目錄 ……………………………………………………………………Ⅶ
第1章 緒論 ……………………………………………………………1
1.1 前言 …………………………………………………………….1
1.2 研究目的及內容 ……………………………………………….1
1.3 研究方法與流程 ……………………………………………….2
第2章 文獻回顧 ………………………………………………………3
2.1 混凝土電阻係數 ……………………………………………….3
2.2 混凝土氣體滲透 ……………………………………………….4
2.3 混凝土吸水率 ………………………………………………….5
2.4 混凝土強度與耐久性 ………………………………………….5
2.5 混凝土滲透性與耐久性 ……………………………………….6
2.6 飛灰 …………………………………………………………….6
2.7 爐石粉 ………………………………………………………….7
2.8 水泥 …………………………………………………………….9
第3章 試驗計畫 ………………………………………………………11
3.1 試驗變數 ……………………………………………………….11
3.2 試驗材料與配比 ……………………………………………….11
3.3 試驗方法 ……………………………………………………….19
第4章 試驗結果與分析 ………………………………………………21
4.1 波特蘭Ⅰ、Ⅱ型水泥混凝土抗壓強度試驗結果 …………….21
4.2 波特蘭Ⅰ、Ⅱ型水泥混凝土吸水率試驗結果 ……………….30
4.3 波特蘭Ⅰ、Ⅱ型水泥混凝土氣體滲透試驗結果 …………….38
4.4 波特蘭Ⅰ、Ⅱ型水泥混凝土電阻係數試驗結果 …………….46
第5章 結論與建議 ……………………………………………………48
5.1 結論 …………………………………………………………….48
5.2 建議 …………………………………………………………….49
參考文獻 …………………………………………………………………50
作者簡介 …………………………………………………………………52

[1]黃兆龍、湛淵源，1999，「飛灰、爐石和矽灰在高性能混凝土使用策略分析」，應用礦物摻料提昇混凝土品質研討會，台灣營建研究院，台北。
[2]ACI Committee 201.2R, 1992, ”Guide to Durable Concrete,” ACI Manual of Concrete Practice, Proc., Vol. 74 , pp. 573-609.
[3]紀茂傑，2002，混凝土耐久性影響因素及評估方法之研究，博士論文，國立臺灣海洋大學，河海工程學系。
[4]Wenner, F. 1915, ”Bulletin of the Bureau of Standards”, V. 12 , pp. 469-478.
[5]劉裕意，2001，添加卜作嵐材料對於混凝土耐久性影響之探討，碩士論文，國立臺灣海洋大學，河海工程學系。
[6]姜乃仁，2004，混凝土耐久試驗新法之研究，碩士論文，國立中興大學，土木工程學系。
[7]Calogovic, V. , 1995, ”Gas Permeability Measurement of Porous Materials (Concrete) by Time-Variable Pressure Difference Method”,Cement and Concrete Research,Vol. 25, No. 5, pp. 1054-1602.
[8]Natalyta Hearn, Gordon Lok, 1998, ”Measurement of Permeability under Uniaxial Compression-A Test Method”, ACI Material Journal ,V. 95, No. 6.
[9]Sanjuan, M. A., Munoz-Martialay R., 1997, ” Variable of the Concrete Air Permeability Coefficient”, Building and Environment, Vol. 32, No. 1, pp. 51-55.
[10]Jacobs, F., 1998, ”Permeability to Gas of Partially Saturated Concrete”, Magazine of Concrete Research, No. 2. pp. 115-212.
[11]顏旭堯，2001，以不同試驗法探討添加卜作嵐材料對混凝土微觀特性影響之研究，碩士論文，國立臺灣海洋大學，材料工程研究所。
[12]林炳炎，1991，飛灰用在混凝土中，現代營建雜誌社，台北。
[13]陳惠鋒，1993，提高飛灰混凝土早期強度策略之研究，碩士論文，國立中央大學，土木工程研究所。
[14]蔡壽楨，2005，含飛灰混凝土之孔隙與強度關係，碩士論文，國立中興大學，土木工程學系。
[15]郭同杉，2005，添加飛灰對混凝土抗壓強度及耐久性影響之探討，碩士論文，國立臺灣海洋大學，河海工程學系。
[16]徐金泉，1998，水淬高爐爐石粉應用於混凝土技術，台灣營建研究院叢書，台北。
[17]陳韋嘉，2005，添加爐石粉對混凝土抗壓強度及滲透行為之探討，碩士論文，國立臺灣海洋大學，河海工程學系。
[18]黃偉翔，2006，卜作嵐材料對不同輕質粒料混凝土力學性質與耐久性質之影響，碩士論文，國立臺灣科技大學，營建工程系。
[19]歐宏毅，2006，添加卜作嵐摻料對於波特蘭Ⅱ型水泥混凝土性質之研究，碩士論文，國立屏東科技大學，土木工程系所。
[20]Roy, D. M. and G. M. Idorn, 1982, “Hydration, Structure, and Properties of Blast Furnace Slag Cements, Mortars, and Concrete,” ACI Journal, Vol. 26, Mar., pp. 444~457.
[21]Sivasundaram, V. and V. M. Malhotra, 1992, “Properties of Concrete Incorporating Low Quantity of Cement and High Volumes of Ground Granulated Slag,” ACI Materials Journal, Vol. 89, No. 6, pp. 554~563.
[22]Osborne, G. J. , 1999, “Durability of Portland Blast-Furnace Slag Cement Concrete,” Cement and Concrete Composites, Vol. 21, pp. 21-29.
[23]黃兆龍，1999，混凝土性質與行為，詹氏書局，台北。
[24]高健章，2000，溫度對混凝土水化反應機理與力學行為之影響，台灣營建研究院橋樑現地蒸汽養生講習班，第91-96頁。
[25]Page, C. L., Short, N. R., and Holden, W. R. , 1986, “ Influence of Different Cements on Chloride-Induced Corrosion of Reinforcing Steel,” Cement and Concrete Research, Vol. 16, No. 1, pp. 79-86.
[26]鄭達鈞，2003，配比參數對自充填混凝土工程性質之影響，碩士論文，國立屏東科技大學，土木工程系。