研究生:劉家成
研究生(外文):Chia Cherng Liu
論文名稱:(一)聚(乙二醇)丙烯酸酯與環氧樹脂互穿網之物性研究(二)不飽和聚酯與環氧樹脂互穿網之物性研究
論文名稱(外文):(1) Study of IPN's Based on PEGDA,PEGMA and Epoxy (2) Study of IPN's Based on UP and Epoxy
指導教授:林木獅
指導教授(外文):M. S. Lin
學位類別:碩士
校院名稱:國立交通大學
系所名稱:應用化學系
學門:自然科學學門
學類:化學學類
論文種類:學術論文
論文出版年:1995
畢業學年度:83
語文別:中文
論文頁數:129
中文關鍵詞:互穿網目網目互鎖效應
外文關鍵詞:Interpenetrating Polymer NetworkNetwork interlock effect
相關次數:
  • 被引用被引用:0
  • 點閱點閱:311
  • 評分評分:
  • 下載下載:0
  • 收藏至我的研究室書目清單書目收藏:0
本文利用 poly ethylene glycol(PEG)及 poly ethylene glycol hyl
ether(PEGME)分別和 acryloyl chloride 反應來合成 Poly(ethylene
glycol)diacrylate (PEGDA200) 及 Poly(ethylene glycol monomethyl
ether)acrylate (PEGMEA500) 做為預備材料, 為硬化劑來形成交聯。同
時和以 IPDA 為硬化劑的環氧樹脂摻混形成 Epoxy/PEGDA 全互穿網及
Epoxy/PEGMEA 半互穿網。另外以 BPO 為不飽和聚酯的交聯劑,加上以
MXDA 為硬化劑的環氧樹脂來作為同部互穿網。而後以 DSC 來測其放熱峰
及 Tg 點的變化, TGA 測其熱性質, FT-IR 測其分子間作用力,黏度計測
其黏度變化特性, RDS 測其動態機械黏彈性質, Tensile ( Instron )
及 Impact ( Falling weight ) 來測其機械性質。

Poly(ethylene glycol monomethyl ether) and Poly(ethylene glycol
monomethyl ether)(PEGME) were used,respectively, to react with
acryliyl chloride to yield Poly(ethylene glycol) diacrylate(
PEGDA) and Poly(ethylene glycol monomethyl ether) acrylate(
PEGMEA). The fully-IPN's based on PEGDA and Epoxy were prepared
by blending PEGDA and epoxy (DGEBA) and were cured simultane-
ous with 2,2'-azo-bisisobutyronitrile(AIBN) and isophronedia-
mine(IPDA).The Semi-IPN's based on PEGMEA and epoxy were same
curing agent.While the other fully-IPN's system based on
unsaturated polyester(UP) and epoxy were prepared by using
benzoyl peroxide(BPO) and m-xylenediamine( MXDA) as curing
agent. The glass transition temperature (Tg) and exothermic
peak shift were determined with differential scaning
calorimeter(DSC). The intermolecular interaction we
investigated with FT-IR. Viscosity increase during IPN form
were measured with a Brookfield viscometer. Dynamic mechani
behaviors were studied with a rheometric dynamic spectrosco
RDS). Tensile-elongation and impact resistance were measured
with an instron tensile test machine and impact tester.