研究生:吳明憲
研究生(外文):Wu, Ming Hsien
論文名稱:環氧樹脂/亞克力樹脂系高分子分散液晶膜之結構特性及熱電光性質
論文名稱(外文):Structure of Epoxy/Acrylate-Based Polymer Dispersed Liquid Crystal Films and the Dependence of the Electrooptical Characteristics on Temperature
指導教授:金惟國
指導教授(外文):Chin, Wei Kuo
學位類別:碩士
校院名稱:國立清華大學
系所名稱:化學工程研究所
學門:工程學門
學類:化學工程學類
論文種類:學術論文
論文出版年:1996
畢業學年度:84
語文別:中文
論文頁數:111
中文關鍵詞:高分子分散液晶膜環氧樹脂/硬化劑當量比電光性質溫度
外文關鍵詞:PDLCepoxy oligomer/hardenerliquid crystalelectrooptic
相關次數:
  • 被引用被引用:1
  • 點閱點閱:586
  • 評分評分:系統版面圖檔系統版面圖檔系統版面圖檔系統版面圖檔系統版面圖檔
  • 下載下載:0
  • 收藏至我的研究室書目清單書目收藏:1
本文主要在探討添加液晶E63的環氧樹脂/亞克力樹脂雙官能性配方系統,
經過紫外光與熱逐步硬化程序,所製備的高分子分散型液晶薄膜(PDLC)
之電光性質及溫度對其電光性質影響。配方中採用三種環氧樹脂與硬化劑
的不同當量比,液晶含量則為40wt%至60wt%。熱硬化條件之選擇乃依據示
差熱分析(DSC)和熱重分析(TGA)掃瞄來判定。PDLC膜中液晶相分離程
度和液晶粒徑、分佈情形,分別由DSC及SEM分析結果來瞭解,並以紫外光
可見光分光度計,測量不同電壓下的穿透度變化。同時利用自製的加熱控
溫裝置,探討不同溫度下之電光性質。實驗結果發現,經紫外光/熱逐步
硬化的薄膜,除印加電場有明暗對比顯示效果外,也可以透過溫度的變化
,達到熱切換顯示效果。

In the research, the polymer dispersed liquid crystal (PDLC)
film was prepared and studied. Formulations used were a mixture
of epoxy oligomer, acrylate oligomer and E63 liquid crystal.
The UV/thermal stepwise curing procedure were used to produce
PDLC film, and the electrooptical characteristics of film were
discussed in different formulations ,including three different
stochiometric ratios of epoxy oligomer/hardener, three
different weights of liquid crystal. Then the film was
subjected to various ambient temperatures to observe electro-
optic changes. The UV and thermal curing condition s were
determined by the studies of DSC, TGA, respectively, The phase
separation degrees of liquid crystal droplets in PDLC film were
discussed by DSC and the sizes of droplets were observed by
SEM. Finally, the spectrophotometer was used to measure the
transmittance of PDLC film in the presence of applied electric
field in various temperatures. These suggest that a PDLC film
can be used as a voltage and temperature sensing material.