研究生:施智騰
研究生(外文):Shy, Jyh Terng
論文名稱:聚合多質子酸先驅物法製備La3CaBa3Cu7Oy超導粉末與物性研究
論文名稱(外文):Preparation and physical properties of La3CaBa3Cu7Oy superconducting powders from polymeric polyprotic acid precursor method.
指導教授:高惠春, 王啟銘
指導教授(外文):Huey-Chuen I.Kao, Chi-Ming Wang
學位類別:碩士
校院名稱:淡江大學
系所名稱:化學學系
學門:自然科學學門
學類:化學學類
論文種類:學術論文
論文出版年:1996
畢業學年度:84
語文別:中文
論文頁數:102
中文關鍵詞:鈦酸鈣多質子酸
外文關鍵詞:pervoskitepolyprotic acid
相關次數:
  • 被引用被引用:0
  • 點閱點閱:222
  • 評分評分:
  • 下載下載:0
  • 收藏至我的研究室書目清單書目收藏:0
本篇論文主要是以聚合多質子酸聚先驅物法來製備含三層鈦酸鈣結構的
La3CaBa3Cu7Oy的次微米超導粉末並研究其物性。以多種多質子酸製備超
導樣品,在聚酯化後,以紅外線光譜分析聚合過程時聚合是否完全,再
以250℃進行熱分解,便得到最初的餅狀先驅物,將這些餅狀先驅物取不
同區域上的點作ICP,並由ICP所得的相對標準偏差看金屬分佈是否均勻,
相對標準偏差小的表示均勻度佳,反之均勻度差;研磨10分鐘後於500℃
預燒2小時後燒掉殘餘的有機物,再將樣品以800℃鍛燒3小時將有機物燒
盡,取其樣品作EDS以瞭解樣品在微觀上的均勻度並以SEM測其粒徑大小,
並以元素分析測樣品在800℃的鍛燒後所剩的C、H、N等的有機物含量,再
以900℃鍛燒數十小時,在400℃氧氣氛中補氧12小時以得到La3CaBa3Cu7
Oy的超導粉末,將其超導粉末作SQUID測其超導轉變溫度及超導含量。並
由XRD來看樣品是否為單相,以瞭解各聚合多質子酸先驅物法所製備的樣
品是否容易形成單相,並比較聚合多質子酸先驅物法中螯合和聚合兩項效
應對於均勻度的影響,結果發現擁有多的羧基和羥基的多質子酸對於螯合
和聚合有較佳的影響而含氮的多質子酸由於本身的胺基會加強其螯合能力
使羧基與金屬離子形成強的鍵結,間接使羧基無法形成有效聚合而影響均
勻度。將各多質子酸先驅物法製成塊材作導電度的測試,以瞭解其超導性
,並比較均勻度與超導性的關係,結果顯示含三個以上羧酸的多質子酸,
可製成較佳的超導體,擁有不錯的超導溫度及導電度,其中以檸檬酸可得
到最好的結果。

In this thesis, submicro superconducting powder of La3CaBa3Cu7
Oy(L3137) are prepared from polymeric polyprotic acid precursor
method. Many different polyprotic acids were used. The sample
after polyesterification was analyzed with IR, and then
pyrolyzed at 250℃ to obtain the pancake-like precursor. The
homogeneity of precursor was determined with ICP, and then the
precursor was precalcined in furnace for 2 h at 500℃ for
further pyrolysis and calcined at 800℃ to decompose the organic
constituents and inorganic salts. The samples was then measured
by EDS to examine microscopic homogeneity and particle size was
measured by SEM. The reaction mixture obtained was ground and
calcined at 900℃ for over ten hours and annealed at 400℃ for 8
h, then L3137 superconducting powders was formed. The single
phase L3137 powder was determined by XRD. The polyprotic acid
with more carboxylic and hydroxy groups exhibited better
chealtion and polyesterfication effects, and gave good
homogeneity. The conductivity of the pellets obtained from
polymeric polyprotic acid precursor method was measured and the
results showed that polyprotic acids with more than three
carboxylic groups are good for formation of superconductor with
high Tc and conductivity. In conclusion, , citric acid gave the
best results among the polyprotic acid used.