研究生:朱俊嘉
論文名稱:交鏈型非線型光學高分子材料--偶氮染料/MMA系統之研究
論文名稱(外文):Cross-Linked Polymer Materials for Nonlinear Optics Cured Acrylic Monomer Bearing Azobenzene Dye
指導教授:李選能
學位類別:碩士
校院名稱:輔仁大學
系所名稱:化學學系
學門:自然科學學門
學類:化學學類
論文種類:學術論文
論文出版年:1997
畢業學年度:85
語文別:中文
論文頁數:67
中文關鍵詞:偶氮染料/MMA系統
外文關鍵詞:Disperse Red 1
相關次數:
  • 被引用被引用:0
  • 點閱點閱:145
  • 評分評分:
  • 下載下載:0
  • 收藏至我的研究室書目清單書目收藏:0

本研究是以Disperse Red 1與Methals chloride先合成 4'-[[[2-(mnethacryloyloxy)ethyl, ethyl]amino]-4-nitroazobenzene (DRIM),然後將DRMMA及交鏈劑I, di (ethylene glycol) dimethacrylate反應交鏈型非線性光學高分子材料。將 DRIM,MMA,交鏈劑IPO混合溶液灌入液晶cell中,施加電場並加熱以完成所需之膜。
另外又將DRI與acryloyl chloride合成4'-[[2-(acryloyloxy)ethyl]ethylamino]-4-nitroazobenzene (DRIA),然後也同樣的將DRIA,MA,交鏈劑II,pentaerythritoltetraacrylate反應形成交鏈型非線性光學高分子材料。
以DSC,TGA測試交鏈劑量,NLO劑量對高分子材質耐熱性質之影響,並探討其SHG強度隨時間及溫度變化之情形。
結果由DSC所得到的值是當交鏈劑愈高其玻璃轉化溫度也愈高,Tg由120℃提升至256℃,而TGA所得的結果也是交鏈劑愈高其裂解溫度也隨之升高,Td由225℃提升至302℃。
所形成的高分子材料在不同溫度層中可得知其衰退程度,當高分子所含交鏈劑越高時,在每個溫度層中其非線性光學性質衰退的越少,越能保持較高的非線性光學效應。當所含的交鏈劑(I)達60wt%時,其非線性光學性質在120℃維持在80%左右,當所含的交鏈劑(Ⅱ)達20wt%時,其非線性光學性質也能維持在70%左右。
同樣的,所形成的高分子材料在恆溫中 (80℃) 時也可測出其衰減情形,結果也是所形成的高分子材料所含的交鏈劑越多時,其非線性光學效應衰減的越少。於長時間測試時含交鏈劑(I) 越高的高分子,其非線性光學性質在經過192小時後仍能維持在60%左右。


A new thermoseting second-order nonlinear optical (NLO) polymer was synthesized from 4'-[[[2-(methacryloyloxy)ethyl]- ethyl]amino]-4-nitroazobenzene (DRIM), MMA, and a crosslinking agent (I), di(ethylene glycol) dimethacrylate. The NLO molecule, DRIM was systhesized from Disperse Red I and methacryloyl chloride. This polymer was then crosslinked by thermal process under electric field poling. The crosslinked polymers containing higher content of crosslinking agent exhibited a higher Tg and Td, and the decay speed of their second-harmonic generation signal also lowered.
From the DSC analyses, the crosslinked polymers depending on the amount of crosslinking agent I exhibited higher Tg values ranging from 120℃ to 256℃, and the Td values also varied from 225℃ to 302℃, as detected by TGA analyses. When the crosslinked polymer containing 60wt% crosslinking agent I, its NLO property can retain up to 80% at 120℃, and can retain up to 60% at 80℃ after 192 hours.
Another thermoseting polymer system was synthesized from 4'-[[2-(acryloyloxy)ethyl]ethyl]ethylamino]-4-nitroazobenzene (DRIA), MA, and crosslinking agent II, pentaerythritol tetraacrylate. With incorporating of 20wt% crosslinking agent II, the NLO property of the crosslinked polymers can remain up to 70% at 120℃.