研究生:簡朝發
論文名稱:聚乙烯之熔融剪切黏度對聚乙烯/改質聚醯胺摻合物之形態、阻隔性及耐衝擊強度之影響
論文名稱(外文):Effects of Polyethylene on the Morphologye, Barrier and Impact Properties of Polyethylene/Modified Polyamide Blends
指導教授:葉正濤
學位類別:碩士
校院名稱:國立臺灣科技大學
系所名稱:纖維及高分子工程技術研究所
學門:工程學門
學類:紡織工程學類
論文種類:學術論文
論文出版年:1997
畢業學年度:85
語文別:中文
論文頁數:92
中文關鍵詞:聚乙烯/改質聚醯胺改質聚醯胺阻隔性耐衝擊強度
外文關鍵詞:Polyethylene/modified polyamidePE/MPABarrierImpact Properties
相關次數:
  • 被引用被引用:0
  • 點閱點閱:204
  • 評分評分:
  • 下載下載:0
  • 收藏至我的研究室書目清單書目收藏:0

本研究針對不同種類之PE熔融剪切黏度對其對應之聚乙烯(polyethylene, PE)/改質聚醯胺(modified polyamide, MPA)摻合物之阻隔性能、衝擊強度及其它相關物性之影響,作一系統性之研究。選用一種含有羧酸(alkylcarboxylic acid)官能基之聚烯烴(Polyolefins)作為相容劑先質(Compatibilizer precursor, CP),以雙螺桿擠壓機進行〝反應性擠壓〞加工來改質聚醯胺(即MPA),並使MPA之阻隔性較純PA佳。結果發現PE之融熔剪切黏度對MPA在PE/MPA摻合物吹瓶過程中之成型形態有極顯著之效應。對於一特定MPA,當此MPA與PE之融熔黏度比(VR)接近一適當範圍值時,在PE/MPA瓶內發現具有最明顯且連續之MPA積層結構。而當其融熔黏度比大於或小於此適當範圍外時,則MPA在PE/MPA摻合瓶內之積層變得破碎且不清晰。此外,這些PE/MPA之摻合瓶之衝擊性能及其對xylene之滲透阻隔性能亦隨VR值增加直至VR值達到一適當範圍之後,其衝擊性質及抗xylens滲透性質隨VR值增加而明顯下降。可能解釋這些有趣現象之原因亦在本研究中討論。


An investigation of the influence of the melt shear viscosities of polyethylenes (PE) on the morphology, barrier and impact properties of polyethylene/modified polyamide PE/MPA bottles is reported. The melt shear viscosities of polyethylenes exhibited a significant influence on the deformation and morphology of MPAs during blow-molding process of polyethylene/modified polyamide (PE/MPA) blends. Some obscure MPA laminars were observed in PE/MPA bottles as the value of melt shear viscosity ratio of MPA to PE (VR) deviated significantly from the "optimum" range. In contrast, clear and elongated laminar structures of MPAs were found as the value of VR reached the "optimum" range. Similarly, the total impact energies (Ets) and permeation barrier properties of PE/MPA samples improved with the value of VR until it reached the "optimum" range, after which value Ets and permeation barrier properties of PE/MPA samples reduced significantly with further increasing VR. Possible mechanisms accounting for these interesting behaviors are presented in this study.