本研究之目的在探討一氧化碳經由不同的二氧化錫奈米顆粒體為感測材料與金梳狀電極為載體之低溫感測器試製與感測特性鑑訂。所建構之氣體偵測器具備歐姆阻抗。利用溶膠-凝膠合成法所製備之二氧化錫奈米顆粒其平均直徑為20nm至50nm。用TEM與XRD檢測感測膜時顯示出二氧化錫奈米顆粒為多晶結構且每個晶粒形狀為矩形，環狀SAD檢測圖形顯示出二氧化錫奈米顆粒體屬於多晶結構。構裝後，實驗所量測輸出之訊號顯示一氧化碳感測訊號靈敏度明顯受操作溫度影響，在350℃時達極大值。平衡輸出訊號與一氧化碳濃度(20-100 ppm）呈線性關係，且由此關係可得一校正曲線。當摻雜鈀(3.5wt %)在二氧化錫奈米顆粒體時，能使感測靈敏度提高約50%，這可能是因為摻雜負電性較錫略高之鈀導致一些缺陷產生在二氧化錫多晶結構上，如此增加更多可用的活位。這些活位能夠與更多氣體分子產生交互作用，因此訊號輸出增加。

This thesis reports investigates on CO sensing due to different sizes of SnO2 nanoparticles as probing material. that were coated on a substrate of comb-type Ag electrode. Sol-gel was synthesized to imbed tin-dioxide nanoparticles with average diameter in a range of 20-50 nm. A gas detection instrument system incorporating our sensing element was set-up for performance evaluation based on signal output implementing the ohmic resistance. Transmission electron spectroscope and X-ray diffraction investigations indicated that the SnO2 nanoparticles grown by sol-gel synthesis process formed crystal clustering of rectangle-like. The scattered ring pattern further confirmed that the SnO2 nanoparticles belonged to polycrystalline structure. Performance test showed that the CO sensing signal sensitivity is obviously influenced by operating temperature, and the optimum condition appeared at 350 °C. A linearity output in respond to CO concentration between 20 and 100 ppm was obtained. This shows that it can be served as a calibration curve. Pd (3.5 wt %) doped into SnO2 nanoparticle clusters was shown to increase in sensitivity of approximately 50%. This is presumably duo to the fact that the more electronegative Pd created some defects in SnO2 polycrystals, thus creating more available active sites for CO sensing and enhanced signal condition.

誌謝 …ii
摘要 ...iii
Abstract ...iv
圖目錄 ...vii
表目錄 ...ix
符號說明 …x

第一章 緒論　
1-1 前言 …1
1-2 研究動機與目的 …3
第二章 文獻探討　
2-1 分子反應動力學理論 …5
2-2 氣體感測器原理與種類 …13
2-3 奈米材料簡介 …28
2-4 奈米微粒簡介 …31
2-5 奈米顆粒體的製備方法 …32
2-6 二氧化錫的材料性質 …36
2-7 半導體式氣體感測器的工作原理 …38
2-8 影響感測性質之因素 …50
2-9 溶膠-凝膠法 …54
2-10 旋轉塗佈法的原理 …58
2-11 設計方法論 …59
第三章 材料與方法
3-1 實驗藥品 …66
3-2 製備SnO2凝膠 …66
3-3 電極與感測器之製備 …68
3-4 感測電路 …69
3-5 樣品之基本物性分析 …70
3-6 氣體感測實驗 …71
第四章 結果與討論
4-1 溶膠凝膠法-製程 …74
4-2 數據分析 …74
4-3 感測溫度對靈敏度的影響 …77
4-4 氣體濃度對感測度的影響 …78
4-5 催化劑的作用對感測靈敏度之影響 …80
第五章 結論與建議
5-1 結論 …83
5-2 建議 …83
參考文獻 …85

1.王瓊紫。2000。以錫修飾白金電極對一氧化碳感測之研究。碩士論文。台南：成功大學化學工程學研究所。
2.王士敏、許祖勳、傅晶。2002。納米材料製備技術。初版, 130-145。北京:化學工業出版社。
3.李世陽。2002。奈米科技對傳統塑橡膠產業發展機會探索。工業材料雜誌材料 185：93-98。
4.卓聰吉。2000。水產養殖用多功能微感測器之設計研究。台北：台灣大學農機所。
5.林嘉龍。2002。設計微溶氧感測器之理論分析與模擬。台北：台灣大學生機所。
6.邱秋燕、周澤川。1993。化學感測器之原理與應用。化工 40(3)：120。
7.周澤川、林宗榮。2002年。臺灣地區石化工廠中之化學感測器使用概況。化學技術 8(2)：116-119。
8.馬振基、江金龍、關旭強、吳岱霖、張文吉。2002。溶凝膠型奈米複合材料之研發與應用。工業材料雜誌材料185:142-149.
9.徐國財、張立德。2002。納米複合材料。初版, 150-170。北京:：化學工業出版。
10.陳一誠。1992。金屬氧化物半導體型氣體感測器。材料與社會 68：62-65。
11.陳正隆、陳幸郎、李志郎。1994。分子動力計算在化學上的應用。化學52(2)：210-214。
12.陳秋岑。1999。真空蒸鍍熱氧化法製備氧化鎵薄膜氣體感測器之研究。碩士論文。台南：成功大學化工系.
13.陳慧英、黃定加、朱秦億。1999。溶膠凝膠法在薄膜製備上之應用。化工技術7(11) :152-166。
14.莊睦賢、黃炳照。2000。氧氣感測器之應用。化工技術 8(2)：168-173。
15.程長遠。1999。分子模擬聚合物分子在固態表面的吸附現象與液態層析法的分離機制。博士論文。台北：淡江化學所。
16.楊明長、曾坤億、王瓊紫。2000。一氧化碳感測器之原理與應用。化工技術 8(2)：158-167。
17.蔡嬪嬪、曾明漢。1992。氣體感測器之簡介、應用及市場。材料與社會 68：50-56.
18.劉吉平、郝向陽編著。2002。納米科學與技術。初版, 10-16,199-200。北京：科學出版社。
19.鄭煜騰、鄭耀宗。1997。氣體感測器的市場分析與發展概況。科儀新知18(5)：76-84。
20.賴耿陽。1992。感測器應用技術。二版,132-145。台北:復漢。
21.蕭明校、羅義興、徐芳儀。1993。高科技奈米化工技術的開發。工業材料197：147-148。
22.Adriani, P. M. and A. K. Chakraborty .1993.Dynamics of relaxation at strongly interacting polymer-solid interface：Effects of chain architecture. J.Chem.Phys 98(5):4263-4274.
23.Barsen, N. and R. Ionescu. 1993. The mechanism of the interaction between CO and an SnO2 surface: the role of water vapor. Sensors and Actuators B 12:71-75.
24.Berberich, M.S., J.G. Zheng, U.Weimar, W.Gõpel, N.Bârsan, E.Pentia and A.Tomescu, 1996. The effect of Pt and Pd surface doping on the response nonocrystalline tin oxide gas sensor to CO. Sensors and Actuators 31:71-75.
25.Broszeit, E., C. Friedrich and G. Berg. 1999.Deposition, properties and application of PVD CrxN coatings. Surface and Coatings Technology 115(1):9-16.
26.Brucker, U. and N. L. Allinger.1982.Molecular Mechanics. Washington, DC: American Chemical Society .
27.Chang, S. C. 1979. Thin-film semiconductor NOx sensor. IEEE Transactionson Electron Devics 26(12):1875-1880.
28.Chen, Q., Y. Qian, G. Zhou and Y. Zhang. 1995. Fabrication of ultrafine SnO2 thin films by the hydrothermal method. Thin Solid Films. 264(1):25-27.
29.Fujita, J. and F. Shimizu. 2002. Atom manipulation using atomic de Broglie waves. Materials Science and Engineering B96(2):159-163.
30.Geistlinger, H. 1993. Electron theory of thin-film gas sensors. Sensors and Actuators B 17:47-60.
31.Gopel W. and K. D. Schierbaum. 1995. SnO2 sensors：current status and future prospect. Sensors and Actuators B 26-27:1-12.
32.Hehre, W. J.,L. Radom, P. V. R. Schleyer and J. A. Pople.1986.Ab Initio Molecular Orbital Theory. New York: John Wiley and Sons .
33.Heiland, G. 1982. Homogeneous semiconducting gas sensors. Sensors and Actuators 2:343-361.
34.Ihokura, K. and J. Watson. 1994. The Stannic Oxide Gas Sensor Principles and Application. 3rd ed., 64-82. Tokyo: CRC Press.
35.Kohl, D. 1989. Surface processes in the detection of reducing gases with SnO2-based devices. Sensors and Actuators 18:71-113.
36.Kruis, F. Einar., H. Fissan, and A. Peled. 1998. Synthesis of Nanoparticles in the Gas Phase for Electronic. Optical and Magnetic Applications—a Review. Journal of Aerosol Science 29(5-6):511-535.
37.Li, D., L. Kong, L. Zhang and X. Yao. 2000. Sol-gel preparation and characterization of transparent KTiOPO4/SiO2 nanocomposite glass for second harmonic generation. Journal of Non-Crystalline Solids 271(1-2):45-55.
38.Levine, Ira N. 1995. Physical chemistry. 4th ed., 443. New York: McGraw-Hill .
39.Mcaleer, J. F., P. T. Moseley, J. O. W. Norris and D. E. Williams. 1987. Tin dioxide gas sensors. Journal of the Chemical Society. Faraday Transactions 83:1323-1346.
40.Morrison, S. R. 1990. The Chemical Physics of Surfaces. 2nd ed., 251. New York: Plenum Press.
41.Morrision, S. R. 1994. Chemical sensors. In “Semiconductor Sensors” , ed. S. M. Sze, 383. New York: John Wiley and Sons.
42.Moseley, P. T. 1992. Materials selection for semiconductor gas sensors. Sensors and Actuators B 6:149-156.
43.Nigel Cross. 1994, Engineering Design Methods, Strategies for Product Design.
44.Ouyang, Y.S. 2003. Inquiry into in-vivo Bio-neutrals Detection Problems. 首屆兩岸科技與經濟論壇論文集，241-247。福建：福州科協。
45.Ouyang, Y.S. 2004. Study on the Functionality of a Histidine Residual. 第三屆兩岸科技與經濟論壇論文集，(II):1-9。台北：台大生命科學院。
46.Pfann, W. G. and H. P. Baltes. 1983. A CMOS magnetic filed sensor. IEEE J. of Solid-State Circuits 18:426-428.
47.Pink, H., L. Treitinger and L. Vite. 1980. Preparation of fast detecting SnO2 gas sensor. Japanese Journal of Applied Physics 19(3)：513-517.
48.Reti, F., M. Fleischer, H. Meixner and J. Giber.1994. Influence of water on the coadsorption of oxidizing and reducing gases on the β–Ga2O3 surface. Sensors and Actuators B18-19:138-142.
49.Sancier, K. M. 1967. ESR evidence of CO oxidation by more than oneoxygen species sorbed on ZnO. Journal of Catalysis 9:331-335.
50.Sokovic, M. and M. Bahor. 1998.On the inter-relationships of some machinability parameters in finish machining with cermet TiN(PVD) coated tools. Journal of Materials Processing Technology 78:163.
51.Sze, S. M. 1994. Semiconductor Sensors. 1st. ed., 388-396. New York：John Wiley and Sons.
52.Takashi, T. 1994. Oxygen sensor. Sensors and Actuators B 14:109-110.
53.Weisz, P. B. 1953. Effects of electronic charge transfer between adsorbate and solid on chemisorption and catalysis. The Journal of Chemical Physics 21(9):1531-1538.
54.Windischmann, H. and P. Mark. 1979. A model for the operation of a thin film SnOx conductance-modulation carbon monoxide sensor. Journal of the electrochemical society 126(4):627-633.
55.Xu,C., J. Tamaki, N. Miura and N. Yamazoe. 1991. Grain size effect on gas sensitivity of porous SnO2-based element. Sensors and Actuators B 3:147-155.
56.Yamazoe, N., J. Fuchigami, M. Kishikawa and T.Seiyama, 1979. Interactions of tin oxide surface with O2, H2O and H2. Surface Science 86:335-344.
57.Yamazoe, N. 1991. New approaches for improving semiconductor gas sensors. Sensors and Actuators B 5:7-19.