摘要
本研究以垂直式布里茲曼法( Vertical Bridgman Method )成長As2Te3單晶的二元化合物。利用X-ray繞射分析(XRD)與穿透式電子顯微鏡(TEM)鑑定結晶構造其單位晶胞之參數a = 14.339 Å，b = 4.006 Å，c = 9.873 Å，α = γ = 90

Abstract
In this study, binary compound arsenic telluride As2Te3 single crystal was grown by vertical Bridgman method. The crystalline structure of As2Te3 was determined by X-ray and transmission electron microscope measurements. According to the structural analyses, As2Te3 crystallizes in a monoclinic crystal structure (space group C2/m) with β=95

圖目錄

圖2.1 As2Te3的單斜晶系結構………………………………………3
圖2.2 As2Te3的層狀結構………………………………..........4
圖2.3 三層結構的As2Te3晶體………………………………………4
圖2.4 As-Te之二元相圖…………………………………………….5
圖2.5 拉曼散射現象………………………………………………….7
圖2.6 瑞利譜線、史托克譜線及反史托克譜線…………………….9
圖3.1 實驗流程圖…………………………………………………….12
圖3.2 封管示意圖…………………………………………………….13
圖3.3 搖擺爐裝置…………………………………………………….14
圖3.4 垂直式布里茲曼長晶系統…………………………….………16
圖3.5 溫度梯度特性曲線圖……….…………………………………16
圖3.6 MODEL ST15 CRYOSTAT低溫系統……………………….....21
圖3.7 實體顯微鏡的樣品接線示意圖……………………………….21
圖3.8 拉曼光譜示意圖……………………………………………….22
圖4.1 金相光學腐蝕影像…………….………………………………23
圖4.2 X光繞射圖譜………………………..……………………….24
圖4.3 電子繞射圖形………………………………………………….28
圖4.4 TEM之能譜圖…………………………………………….…..28
圖4.5 FE-SEM之二次電子拋光影像………………………..………33
圖4.6 FE-SEM之二次電子層狀結構影像…………………..……..34
圖4.7 FE-SEM之內層橫截面結構影像……………………………..34
圖4.8 FE-SEM之能譜圖…………………………………..………..35
圖4.9 DSC曲線圖………………………………………..………….36
圖4.10 TGA曲線圖…………………………………………………..38
圖4.11 電阻值與絕對溫度曲線圖……………………………………39
圖4.12 拉曼光譜………………………………………………………40

表目錄

表2.1 As2Te3晶體結構資料…………………………………………6
表3.1 元素配重表………………………………………….…………13
表3.2 爐體每上升0.5cm所測量的爐內溫度……………………....17
表3.3 晶體成長的參數值…………………………………………...17
表4.1 X光繞射儀之量測結果…………….....................25
表4.2 As2Te3之database…………………………………………..26
表4.3 TEM之參數值………………………………………….......29
表4.4 EPMA之atomic ratio量測結果………………………......31表4.5 EPMA之weight percent量測結果………………………....32
表4.6 DSC之參數值……………...…………………………………37
表4.7 TGA之參數值……………...………………...…………….38

第六章 參考文獻
【1】F. Shimojo, S. Munejiri and K. Hoshino, Journal of Non- Crystalline Solid, 312, 349 (2002).
【2】R. Kaplan, Solar Energy Materials and Solar Cells, 85, 545 (2005).
【3】V. Vassilev, S. Parvanov, T. Hristova-Vasileva, L. Aljihmani, Vachkov and T. Vassileva-Evtimova, Materials Letters, in press, (2006) .
【4】B. Bilen, Y. karlatos and G. Aktas, Journal of Non-Crystalline solid, 351, 2153 (2005).
【5】A. Elshafie, B.A. Mansour and A. Abdel, Journal of Physics and Chemistry of Solids, 60, 483 (1999).
【6】S. Mahadevan and A. Giridhar, Journal of Non-Crystalline Solids, 258, 207 (1999).
【7】A. Giridhar, and S. Mahadevan, Journal of Non-Crystalline Solids, 238, 225 (1998).
【8】S. Mahadevan and A. Giridhar, Journal of Non-Crystalline Solids, 221, 281 (1997).
【9】P. E. Lippens, E. Brousse, J. Olivier, A. Gheorghiu and C. Senemaud, Journal of physics and Chemistry of Solid, 62, 467 (2001).
【10】J. M. Durand, Journal of Non-Crystalline Solids, 194, 109 (1996).
【11】T. J. Scheidemantel and J. V. Badding, Solid State Communications, 127, 667 (2003).
【12】http://webmineral.com/data/Orpiment.shtum1(2005).
【13】http://www.webelements.com (2005).
【14】Eugen Tarnow, A. Antonelli, and J. D. Joannopoulos, Physical Review B 34, 4059 (1986).
【15】Binary Alloy Phase Diagrams, T. B. Massalaki, (ASM International, 1990).
【16】Introductory Raman Spectroscopy, R. Ferraro (Academic Press, Boston, 1994).
【17】儀器學, 蘇青森， 五南出版社 (2002).
【18】實用儀器分析，王明光， 合記出版社 (2003).
【19】雷射技術原理實務， 秋葉稔光， 復漢出版社有限公司 (2001).
【20】Raman Spectroscopy For Chemical Analysis, J. D. Winefordner (John Wiley & Sons, New York, 2000).
【21】Raman Scattering in Materials Science, W. H. Weber, R. Merlin (Springer, Berlin, 2000).
【22】Infrared and Raman Spectra of Inorganic and coordination compounds, Nazuo Nakamoto (Wiley, New York, 1997).
【23】儀器分析， 孫逸民，全威圖書有限公司 (1998).
【24】儀器分析，王應瓊，中央圖書出版社出版 (1997).
【25】近代光學大學科學叢書, 李冠卿, 聯經出版社 (1988).
【26】賴錦榮, 「Cd-Yb準晶體與三元Al70Pd22.5Re7.5準晶體之熱電性質」國立東華大學, 碩士論文，民國九十三年
【27】儀器分析， 趙學范， 北京大學出版社 (1994).
【28】儀器分析，孫逸民, 全威圖書有限公司 (1998).