本研究中使用新穎溶膠凝膠法合成純相摻雜鈰之釔鋁石榴石(YAG:Ce)粉末並搭配boehmite為鋁源，由XRD結果顯示經過煅燒1000℃且持溫30min，即可合成純相YAG粉體，由SEM與TEM結果顯示YAG粉體粒徑約於100 nm左右，由實驗結果得知，以本實驗室所改良之溶膠凝膠新方法，可以在低溫短時間合成純相且具良好螢光強度的釔鋁石榴石粉末。

In this research, cerium doped yttrium aluminum garnet (YAG:Ce) powder was successfully synthesized at a low temperature for a short time by novel sol-gel reaction method and used boehmite as the aluminum source. The XRD results shown that the formed powder formed at 1000℃ for 30 min was pure YAG-phase. The SEM and TEM results shown that the product was about 100 nm in diameter. According to the experiment results, the pure garnet phase with high emission intensity powder was formed at low temperature for a short time.

摘要 i
ABSTRACT ii
致謝 iii
目錄 iv
圖表目錄 vi
第一章 緒論 1
1.1前言 1
1.2文獻回顧 3
1.3研究動機 6
第二章 相關原理 7
2.1螢光材料原理及性質 7
2.1.1螢光原理 7
2.1.2發光材料之類型 8
2.2螢光粉之種類 10
2.3 YAG粉體之介紹 11
2.4螢光粉之應用 11
2.5發光二極體之介紹 16
2.6粉體製備方法之介紹 19
2.6.1水熱法 19
2.6.2噴霧裂解法 19
2.6.3共沉澱法 19
2.6.4化學氣相反應法 20
2.6.5固相反應法 20
2.6.6溶膠凝膠法 20
第三章 實驗部分 21
3.1藥品 21
3.2實驗分析儀器 22
3.3實驗方法與實驗步驟 24
3.3.1 傳統固相反應法 24
3.3.2 新穎固相反應法 24
3.3.3新穎溶膠凝膠法 24
第四章 結果與討論 29
4.1不同鋁來源合成YAG粉體之研究 29
4.1.1以傳統固相反應法搭配不同鋁來源之研究 29
4.1.2以新穎固相反應法搭配不同鋁來源之研究 29
4.2傳統固相反應法合成YAG粉體之研究 34
4.3新穎溶膠凝膠法合成YAG粉體之研究 36
4.3.1預陳化pH值對合成YAG粉體的影響 36
4.3.2煅燒溫度對粉體的影響 47
第五章 結論 57
參考文獻 59

[1]S. Roy, L. Wang, W. Sigmund, F. Aldinger, Materials Letters 39 (1999)
138-141.
[2]劉如熹、王健源編著，“白光發光二極體製作技術-21 世紀人類的新曙光”，
全華科機圖書股份有限公司，2001年10 月，pp.1-126。
[3]J. E. Geusic and L. G. V. Uitert, “Laser Oscillations in Nd-dopped Yttrium
Aluminum, Yttrium Gallium and Gadolinium Garnets”, Applied Physics Letter
4(1964)182.
[4]羅浚仁，“照明用螢光粉”，電機月刊，2002年5月，第十二卷，五期，
pp.165-175.
[5]J. McKittrick, L. E. Shea, C. F. Bacalski, E. J. Bosze, “ The influence of
processing parameters on luminescent oxides produced by combustion
synthesis”, Displays 19 (1999) 169-172.
[6]G. Del Rosarioa, S. Oharab, L. Mancicc, Applied Surface Science 238 (2004)
469-474.
[7]J. Yum, S. Kim, Y. Sung, Colloids and surfaces A：Physicochem. Eng. Aspects
251 (2004) 203-207.
[8]M. K. Ashurov, A. F. Rakov and R. A. Erzin, Solid State communications 120
(2001) 491-494.
[9]蔡富州，“以熔鹽法合成釔鋁石榴石單晶粉末之研究”，國立成功大學礦冶及
材料科學研究所碩士論文，1990年7月，pp.1-22.
[10]D. Matusch, “Phasenuntersuchungen in System Y-Si-Al-O-N”, Universitat
Stuttgant Dissertation (2003) 1-82.
[11]E. Mete, “Electronic properties of transition metal oxides”, Natural and Applied
Sciences of The Middle East Technical ( 2003) 1-91.
[12]王明發，“YAG 螢光粉體的製備及其性質”，南台科技大學化學工程研究
所碩士論文，2004年6月，pp.1-10.
[13]M. K. Karin, M. Joanna, “Phase Development and Luminescence in Chromium
-Doped Yttrium Aluminum Garnet (YAG:Cr) Phosphors”, Journal Am. Ceram.
Soc 77 (1994) 2866-2872.
[14]F. Qiu, X. Pu, J. Li, X. Liu, Y. Pan, J. Guo, “Thermal behavior of the YAG precursor prepared by sol-gel combustion process”, Ceramics International 31 (2005) 663-665.
[15]V. B. Glushkova, O. N. Egorova, V. A. Krzhizhanovskaya, K. Yu. Merezhinskill,
“Synthesis of yittrium aluminates by precipitatuin of hydroxides”, Plenum Publishing Corporation UDC 546 (1984) 1015-1018.
[16]A. Ikesue and I. Furusato, “Fabrication of polycrystalline,Transparent YAG ceramics by a solid-state reaction method”, J. Am. Ceram. Soc 78 (1995) 225-228.
[17]Z. Sun, D. Yuan, X. Duan, X. Wei, H. Sun, C. Luan, Z. Wang, X. Shi, D. Xu, M. Lv, “Preparation and characterization of Co2+-doped Y3Al5O12 nano-crystal powders by sol-gel technique”, Journal of Crstal Growth 206 (2004) 171-175.
[18]L. Wena, X. Suna, Z. Xiua, S. Chenb, C. T. Tsaib, “Synthesis of nanocrystalline yttria powder and fabrication of transparent YAG ceramics”, Journal of the European Ceramic Society 24 (2004) 2681–2688.
[19]傅玟娟，“以固相反應法合成YAG 之研究”，南台科技大學化學工程研究
所碩士論文，2006年6月，pp.1-65.
[20]C. Q. Li, H. B. Zuo, M. F. Zhang, J. C. Han, S. H. Meng, “Fabrication of transparent YAG ceramics by traditional solid-state-reaction method”, Nonferrous Met. Soc. China 17(2007) 148-153.
[21]M .S. Tsai, W. C. Fu, W. C. Wu, C. H. Chen, C. H. Yang, “Effect of the aluminum source on the formation of yttrium aluminum garnet (YAG) powder via solid state reaction”, Journal of Alloys and Compounds 455 (2008) 461–464.
[22]Z. Wu , X. Zhang, W. He, Y. Du, N. Jia, G. Xu, “Preparation of YAG:Ce spheroidal phase-pure particles by solvo-thermal method and their photoluminescence”, Journal of Alloys and Compounds 468 (2009) 571–574.
[23]N. Jia, X. Zhang, W. He, W. Hu, X. Meng, Y. Du, J. Jiang, Y. Du, “Property of YAG: Ce phosphors powder prepared by mixed solvothermal method”, Journal of Alloys and Compounds 509 (2011) 1848–1853.
[24]C. W. Won, H. H. Nersisyan, H. I. Won, J. H. Lee, K. H. Lee, “Efficient solid-state route for the preparation of spherical YAG:Ce phosphor particles”, Journal of Alloys and Compounds 509 (2011) 2621–2626.
[25]S. Nishiura, S. Tanabe, K. Fujioka, Y. Fujimoto, “Properties of transparent Ce:YAG ceramic phosphors for white LED”, Optical Materials 33 (2011) 688–691.
[26]石景仁，“白光發光二極體用之石榴石螢光粉合成及特性分析”，國立台灣大學化學研究所碩士論文，2001年6月，pp.1-126.
[27]陳昱霖，“石榴石(Y3Al5O12)螢光體之合成與性質研究”，國立成功大學材
料科學與工程研究所碩士論文，2000年6月，pp.1-109.
[28]劉如熹、劉宇恒編著，“發光二極體用氧氮螢光粉介紹”，全華科技圖書股份有限公司，2006年11月，pp.1-26.
[29]吳欣融，“以新穎溶膠凝膠法製備YAG粉體之性質研究”，南台科技大學化學工程研究所碩士論文，2008年6月，pp.1-69.
[30]黃渝晨，“硫化鋅共摻雜銅、錳之發光特性研究”，逢甲大學化學工程學系碩士論文，2003年，pp.1-70.
[31]G. Blasse and B. C. Grabmaier, “Luminescent Materials”, Springer Verlag, Berlin Heidelberg, Germany (1994).
[32]羅浚仁，“照明用螢光粉”，電機月刊，2001年5月，第十二卷，五期，pp.165-175.
[33]紀喨勝，“紫外光發光二極體用新穎螢光材料之研發”，國立台灣大學化學
研究所碩士論文，2002年6月，pp.1-161.
[34]楊素華編著，“螢光粉在發光上的應用＂，科學發展，2002年10 月，358期，pp.66-71.
[35]李啟瑋，“鋁酸鍶鈣螢光粉體之製備及其光性質研究”，國立成功大學材料科學及工程研究所碩士論文，2006年6月，pp1-84.
[36]王列松，“噴霧熱解法製備Eu3+摻雜的球形發光粉”，中國科學院長春應用化學研究所碩士論文，2004年。
[37]Z. Li, J. Zeng, C. Chen, Y. Li, “Hydrothermal Synthesis and Luminescent Properties of YBO3:Tb3+ Uniform Ultrafine Phosphor”, Journal of Crystal Growth 2 (2006) 286.
[38]郭政男，“以水熱法合成(Ba1-xCax)(Ti1-yZry)O3奈米粉末之研究”，國立成功大學資源工程研究所碩士論文，2005年7月，pp1-75.
[39]W. J. Dawson, “Hydrothermal Synthesis of Advanced Ceramic Powders”, Ceram.
Bull 67 (1988) 1673-1678.
[40]C. H. Lu, S. Y. Lo, P. Y. Yeh, “Hydrothermal Synthesis of Potassium Niobate Powders”, J. Chin. Colloid & Interface Soc 6 (2004) 151-156.
[41]U. Fluckiger, H. Arend, H. R. Oswald, J. Am. Ceram. Soc. 56 (1977) 575.
[42]陳嘉民，“微波輔助溶液燃燒合成法製備螢光粉體”，國立成功大學化學工程 研究所碩士論文，2005年7月，pp.1-116.
[43]I. W. Li, K. O. Li, B. P. Seung and C. K. Yun, Mater. Res. Bull 35 (2000) 789。
[44]石明哲，“晶種對YAG 粉末之生成影響研究”，國立成功大學資源工程研究所碩士論文，2006年6月，pp.1-50.
[45]H. Wang, L. Gao, K. Niihara, “Synthesis of nanoscaled yttrium aluminum garnet
powder by the co-precipitation method”, Materials Sci. Eng 288 (2000) 40- 41.
[46]D. V. Ligia, B. S. Elizabeth and R. D. Marian, “Prearation and characterization of uniform spherical particles of Y2O2S and Y2O2S:Eu”, Jourmal of Materials Chemistry 7 (1997) 2113-2116.
[47]T. Hirai and T. Orikoshi, “Preparation of yttrium oxysulfide phosphor nanoparticles with infrared-to-green and blue upconversion emission using an emission liquid membrane system”, Journal of Colloid and Interface Science 273 (2004) 470-477.
[48]賴佳芸，“氧化釔粉末粒徑對YAG生成活化能之影響”，國立成功大學資源工程研究所碩士論文，2005年7月，pp.1-45.
[49]楊智量，“藉pH值控制混合之固相反應製備的YAG：Ce 粉體分析及其螢光性質”，國立成功大學資源工程研究所碩士論文，2005年6月，pp1-97.
[50]D. J. Robbins, “The effect of crystal field and temperature on the photoluminescence excitation efficiency of Ce3+ in YAG”, Journal of Electrochemical Society 126 (1979) 1550-1555.
[51]葉辰芝，“以明礬合成氧化鋁粉體之研究”，南台科技大學化學工程研究所碩士論文，2007年 6月，pp.1-71.
[52]Y. Zhou, J. Lin, M. Yu, S. Wang, H. Zhang, “Synthesis-Dependent luminescence properties of Y3Al5O12:Re(Re=Ce, Sm, Tb) phosphors”, Materials Letters (2002) 628-636.
[53]P. Colomban, “Structure of oxide gels and glasses by infrared and raman scattering”, Journal of Materials Science 24 (1989) 3002-3010.