本研究中以目前市售4種UNIDYNE、PHOBOL RSH、FG-683E、3M Scotchgard減碳氟素撥水劑對於公司的產品100%PET 75D/72F*75D/72F梭織布與100% Nylon 6 70D/72F*160D/96F 梭織布探討以其撥水劑不同濃度下與定型溫度對於其水洗烘乾10回與20回後其撥水度與各項其物性需要功能之最佳及最適合之條件。其實驗結果得知，從撥水度、柔軟度、成本效益方面得知UNIDYNE撥水劑是最佳的選擇；若是以水洗20回撥水度而言則PHOBOL RSH會是最佳的選擇。且其物性皆可達到市場要求。

This study used the currently marketed four kinds of UNIDYNE、PHOBOL RSH、FG-683E、3M Scotchgard reduce carbon fluoride water repellant agents for the company's products,100% polyester fiber woven fabric 75D/72F * 75D/72F and 100% polyamide 70D/72F * 160D/96F woven fabrics, then using different concentrations of water repellant agents and its setting temperature for washing 10 times after drying and 20 times after drying its water repellant level and the physical properties of the best and most suitable conditions. From water repellency, flexibility,cost-effectiveness knows UNIDYNE repellant agents is the best choice, If washed 20 times after drying, PHOBOL RSH would be the best choice. And physical properties are also match the market requirement.

內容目錄
摘要......................................................................I
Abstract................................................................ II
誌謝..................................................................... Ⅲ
內容目錄…..................................................................Ⅳ
圖目錄....................................................................Ⅶ
表目錄....................................................................Ⅸ

第一章 前言..............................................................1
1-1研究背景…………………………....................................................1
1-2含氟撥水劑的製程方法....................................................2
1-3 法規與限制...........................................................4
1-4 研究目的.............................................................7

第二章 理論...............................................................9
2-1全氟辛烷磺酸鹽(Perfluorooctane sulfonate)..............................9
2-2全氟辛酸(Perfluoroctanoic Acid)......................................10
2-3全氟丁基磺酸(Perfluorobutane sulfonic acid 簡稱PFBS)..................11
2-4全氟己基磺酸(Perfluorohexane Sulfonic acid簡稱PFHS)...................11
2-5聚酯纖維(Polyester fiber, 對苯二甲酸乙二酯)............................11
2-6聚醯胺纖維(polyamide fibre, Nylon)................................12
2-7撥水原理............................................................13

第三章 實驗............................................................15
3-1實驗材料..........................................................15
3-2實驗儀器設備與方法.................................................15
3-3 實驗流程圖......................................................28

第四章 結果與討論....................................................29
4-1 UNIDYNE撥水劑濃度之影響 ........................................29
4-1.1不同濃度對聚酯纖維潑水度之影響...................................29
4-1.2不同濃度對聚醯胺纖維撥水度之影響..................................30
4-2 PHOBOL RSH撥水劑濃度之影響.......................................31
4-2.1不同濃度對聚酯纖維潑水度之影響....................................32
4-2.2不同濃度對聚醯胺纖維撥水度之影響..................................33
4-3 FG-683E撥水劑濃度之影響..........................................34
4-3.1不同濃度對聚酯纖維潑水度之影響....................................34
4-3.2不同濃度對聚醯胺纖維撥水度之影響...................................35
4-4 3M Scotchgard撥水劑濃度之影響....................................36
4-4.1不同濃度對聚酯纖維潑水度之影響....................................37
4-4.2不同濃度對聚醯胺纖維撥水度之影響..................................38
4-5 UNIDYNE撥水劑定型溫度之影響.......................................38
4-5.1不同溫度對聚酯纖維潑水度之影響....................................39
4-5.2不同溫度對聚醯胺纖維撥水度之影響.................................40
4-6 PHOBOL RSH撥水劑定型溫度之影響...................................41
4-6.1不同溫度對聚酯纖維潑水度之影響...................................41
4-6.2不同溫度對聚醯胺纖維撥水度之影響..................................42
4-7 FG-683E撥水劑定型溫度之影響.......................................43
4-7.1不同溫度對聚酯纖維潑水度之影響....................................44
4-7.2不同溫度對聚醯胺纖維撥水度之影響.................................45
4-8 3M Scotchgard撥水劑定型溫度之影響................................46
4-8.1不同溫度對聚酯纖維潑水度之影響...................................46
4-8.2不同溫度對聚醯胺纖維撥水度之影響.................................47
4-9 各環保撥水劑其最適定型溫度與濃度之分析比較............................48
4-10 柔軟度........................................................51
4-11其他物性測試....................................................52
第五章結論.........................................................57
參考文獻...........................................................60

1. 史亞利、潘媛媛、王杰明、蔡亞岐，全氟化合物的環境問題，化學進展，369-376(2009)。
2. 李維豐，全氟辛烷磺酸鹽有效管理制度與策略之研究以臺灣為例，
國立中央大學環境工程研究所碩士在職專班論文，1-4(2006)。
3. 章杰，含氟多功能織物整理劑及其生態問題，印染行業“四新”技術交流會論文集，20—24(2007)。
4. 章杰、張曉琴，禁用含氟表面活性劑及其整理劑的新型替代品，染料與染色，第46卷，第三期，50-52(2009)。
5. 章杰、張曉琴，列入POPs的紡織用含氟表面活性劑及新型替代品，印染助劑，第26卷，第二期，2(2009)。
6.林俊宏，環保型撥水劑發展概況，紡織綜合研究期刊，第17卷，第十二期，69-70(2009)。
7. SAMANTHA WRIGHT 、RICHARD ELSMORE,REACH: getting to grips with SVHC and authorization,Chimica oggi,30(1),49-50(2012).
8. 陳榮圻，REACH法規與印染助劑中的高度關注物質(四)，印染助劑，第35卷，第八期，45-46(2009)。
9. 楊棟樑，PFOS的禁用與含氟防護整理的動向，染料與染色，26-27(2007)。
10. A.M. El-Naggar, Water resistance and surface morphology of syntheticfabrics covered by polysiloxane/acrylate followed by electron beam,irradiation, Nuclear Instruments and Methods in Physics Research B201, pp595-603, 2003.
11. 石天威，撥水抗靜電雙效織物整理加工製程之研究，逢甲大學紡織工程研究所碩士論文，13-14(2005)。