我們以紅外光反射光譜來研究低矽鈣鋁矽氧化物玻璃的結構。在鈣鋁比固定為1.5的氧化物玻璃樣品中，隨著矽含量的不同，使得玻璃結構中的矽的角色發生了改變。經由紅外光反射光譜所得的橫向(TO)及縱向(LO)光譜有助於我們對於玻璃結構的分析。因為在學長超聲波聲速量測實驗中，當矽含量為15mol%時出現了極大值與Higby的Tg model結論下的極值位置不同。為了更進一步釐清矽含量的改變對於玻璃結構的影響，我們試著統合紅外光光譜、拉曼光譜以及超聲波聲速量測實驗做更深入的探討。

The structures of low-silica calcium alumino-silicate oxide glasses were investigated by infrared reflectivity. The role of silica in glass network changes with its composition as a function of the ratio of CaO/Al2O3. Kramers-Kronig analysis was performed on IR reflectivity data to extract longitudinal and transverse optic phonon frequencies. In the previous studied of our Ultrasonic measurement, there were a maximum velocity in the glass with 15mol% silica. These were different from the maximum of Tg model studied by Higby. In order to distinguish the role of silica from the glass network as various contents of silica, we tried to synthesize Infrared spectra, Raman spectra and Ultrasonic measurement to get further information.

目錄
致謝
摘要
Abstract
目錄 I
圖索引 IV
表索引 VI
第一章　簡介 1
第二章　紅外光光譜理論 4
2-1　近似的量子理論 4
2-1-1　The Harmonic Oscillator Model 4
2-1-2　紅外光的選擇定則 8
2-1-3　振動的微擾理論 10
2-2　紅外光光譜 12
2-2-1　紅外光反射光譜 12
2-3　Kramers-Kronig transformation（K-K轉換式） 17
第三章　紅外光實驗裝置及方法 21
3-1　實驗儀器設備 22
3-2　玻璃的紅外光吸收及反射光譜實驗 28
3-2-1　吸收光譜 28
3-2-2　反射光譜 30
3-3　紅外光高溫裝置簡介 33
3-4　玻璃樣品成分與處理方式 37
第四章　實驗結果 39
4-1　常溫紅外光穿透光譜 39
4-2　常溫紅外光反射光譜 41
4-3　常溫紅外光TO、LO光譜 45
4-4　變溫中紅外光反射光譜 55
第五章　實驗討論 57
5-1　常溫紅外光反射光譜實驗結果討論 58
5-2　橫向(TO)與縱向(LO)光學振動模 65
5-3　變溫紅外光反射光譜實驗結果討論 67
5-4　低矽鈣鋁矽氧化物玻璃結構綜合討論 69
第六章　結論 73
參考資料 75

參考資料
1. H. C. Hafner, N. J. Kreidl, and R. A. Weidel, J. Am. Ceram. Soc, 41. 315(1958).
2. J. R. Davy, Glass Technol, 19. 32(1978).
3. P. L. Higby, R. J. Ginther, I. D. Aggarwal, and E. J. Friebele, J. Non-Cryst. Solids, 126 . 209(1990).
4. M. E. Lines, J. Appl. Phys. 60. 1472(1986).
5. M. E. Lines, J. Non-Cryst. Solids. 103. 279(1988).
6. M. E. Lines, J. B. MacChesney, K. B. Lyons, A. J. Bruce, A. E. Miller, and K. Nassau, J. Non-Cryst. Solids, 107. 251(1989).
7. L. G. Hwa, C. C. Chen, and S. L. Hwang, Chin. J. Phys, 35. 78(1997).
8. L. G. Hwa, J. Raman Spectro. 29. 269(1998).
9. P. F. MacMillan, and B. Piriou, J. Non-Cryst. Solids, 55. 221(1983).
10. C. I. Merzbacher, K. J. McGrath, and P. L. Higby, J. Non-Cryst. Solids, 136. 249(1991).
11. C. I. Merzbacher, and W. B. white, J. Non-Cryst. Solids, 130. 18(1991).
12. P. Tarte, Spectrochim. Acta, 23A. 2127 (1967).
13. C. Huang, and E. C. Behrman, J. Non-Cryst. Solids, 128. 310 (1991).
14. J. E. Shelby, J. Am. Ceram. Soc. 68. 155(1985).
15. P. L. Higby, L. E. Busse, and I. D. Aggrawal, Mat. Sci. Forum. 67&68. 155 (1991).
16. M. L. Baesso, A. C. Bento, L. C. M. Miranda, D. F. de Souza, J. A. Sampaio and L. A. O. Nunes, J. Non-Cryst. Solids, 276. 8(2000).
17. J. A. Sampaio, M.L. Baesso, S. Gama, A.A. Coelho, J.A. Eiras, I.A. Santos, J. Non-Cryst. Solids, 304. 293(2002).
18. L. G. Hwa, S. L. Hwang and L. C. Liu, J. Non-Cryst. Solids, 238. 193(1998).
19. L. G. Hwa, and G. W. Lee, Mat. Chem. Phys. 58. 191(1999).
20. L.G. Hwa, K.J. Hsieh, L.C. Liu, Mat. Chem. Phys. 78. 105 (2002).
21. J. L. McHale, Molecular spectroscopy P.248-268, (1999). Prentice Hall
22. 以拉曼散射來研究鑭鋁矽氧化物玻璃之結構，輔仁大學物理研究所郭仲淵碩士論文, P.50-51, (2002年6月)
23. L. Galeener and G. Lucovsky, Structure and Excitation of Amorphous Solids, P.223-228.
24. J.E. Shelby, J. Am. Ceram. Soc, 68. 158(1985).
25. P.L. Higby, R.J. Ginther, I.D. Aggarwal and E.J. Friebele, J. Non-Cryst. Solids. 126. 213(1990).
26. P. Tarte , Spectrochim. Acta. 23A: 2127(1967).
27. P. McMillan, B. Piriou and A. Navrotsky, Geochim. Cosmochim. Acta. 46. 2021(1982)
28. D.E. Day, G.E. Rindone, J. Am. Ceram. Soc. 45. 489 (1962).
29. V.A. Kolesova, Struct. Glass. 2. 177 (1960)
30. B. Mihailova, L. Konstantinov, E. Dinolova, J. Non-Cryst. Solids. 191. 79.(1995).
31. 以拉曼散射來研究低矽鈣鋁矽氧化物玻璃之結構及其中程有序的問題, 輔仁大學物理研究所陳龍勝碩士論文, P.48-51, (2000年6月)
32. 低矽鈣鋁矽氧化物玻璃在便溫及變壓下彈性性質研究, 輔仁大學物理研究所謝國榮碩士論文, P.41, (2002年6月)